The optimum coating composition of alkali Fe powder welding rods was designed by orthogonal experiment with mix rates. A new kind of effective RE-Fe powder welding rod was prepared which could be used at the condition...The optimum coating composition of alkali Fe powder welding rods was designed by orthogonal experiment with mix rates. A new kind of effective RE-Fe powder welding rod was prepared which could be used at the condition of direct and indirect current. The arc characteristics and stabilities of effective Fe powder welding rods containing RE were analyzed by HANNOVER analyzer. The efficiency of Fe powder welding rods was tested by weighting method. It was found that the stability of Fe powder welding rods was improved when it was added with rare earths. The results of impact experiment at low temperatures and SEM analysis on impact break showed that the grain was refined, the welding joint was cleaned, and the mechanical properties of joint was enhanced with proper RE content. It was provided with good processing property for this effective RE-Fe powder welding rod, and its efficiency could arrive at 180%.展开更多
Effects of molten state of ultrasonic welded joints of plastics on their strength were investigated. Physical parameters such as temperature, viscosity and thickness of melting layers of plastic material joints were m...Effects of molten state of ultrasonic welded joints of plastics on their strength were investigated. Physical parameters such as temperature, viscosity and thickness of melting layers of plastic material joints were measured and analyzed. Results show that when the welding vibration amplitude and pressure increase, the temperature increases, the viscosity decreases, and the thickness of molten layer decreases. The microstructure of weld fusion zone was observed by using an optical microscope. It was found that there is strong orientation along transverse direction in the microstructure of fusion zone. Testing results show that the mechanics performance of welded joints are obviously anisotropic, and strongly affected by the thickness of molten layer and the extent of orientation.展开更多
文摘The optimum coating composition of alkali Fe powder welding rods was designed by orthogonal experiment with mix rates. A new kind of effective RE-Fe powder welding rod was prepared which could be used at the condition of direct and indirect current. The arc characteristics and stabilities of effective Fe powder welding rods containing RE were analyzed by HANNOVER analyzer. The efficiency of Fe powder welding rods was tested by weighting method. It was found that the stability of Fe powder welding rods was improved when it was added with rare earths. The results of impact experiment at low temperatures and SEM analysis on impact break showed that the grain was refined, the welding joint was cleaned, and the mechanical properties of joint was enhanced with proper RE content. It was provided with good processing property for this effective RE-Fe powder welding rod, and its efficiency could arrive at 180%.
基金the National Natural Science Foundation of China (No.59675054) andNational Key Laboratory of Advanced Welding Production Techn
文摘Effects of molten state of ultrasonic welded joints of plastics on their strength were investigated. Physical parameters such as temperature, viscosity and thickness of melting layers of plastic material joints were measured and analyzed. Results show that when the welding vibration amplitude and pressure increase, the temperature increases, the viscosity decreases, and the thickness of molten layer decreases. The microstructure of weld fusion zone was observed by using an optical microscope. It was found that there is strong orientation along transverse direction in the microstructure of fusion zone. Testing results show that the mechanics performance of welded joints are obviously anisotropic, and strongly affected by the thickness of molten layer and the extent of orientation.