A series of CuSO4/TiO2 catalysts were prepared using a wet impregnation method.The activity of each sample in the selective catalytic reduction of NO by NH3（NH3-SCR） was determined.The effects of SO2 and H2O,and the...A series of CuSO4/TiO2 catalysts were prepared using a wet impregnation method.The activity of each sample in the selective catalytic reduction of NO by NH3（NH3-SCR） was determined.The effects of SO2 and H2O,and their combined effect,on the activity were examined at 340 ℃ for 24 h.The catalysts were characterized using N2 adsorption-desorption,X-ray diffraction,X-ray photoelectron spectroscopy,temperature-programmed reduction of H2（H2-TPR）,temperature-programmed desorption of NH3（NH3-TPD）,and in situ diffuse-reflectance infrared Fourier-transform spectroscopy（DRIFTS）.The CuSO4/TiO2 catalysts had good activities,with low production of N2O above 340 ℃.SO2 or a combination of SO2 and H2O had little effect on the activity,and H2O caused only a slight decrease in activity during the experimental period.The NH3-TPD and H2-TPR results showed that CuSO4 increased the amounts of acid sites and adsorbed oxygen on the catalyst.In situ DRIFTS showed that the NH3-SCR reaction on the CuSO4/TiO2 catalysts followed an Eley-Rideal mechanism.The reaction of gaseous NO with NH3 adsorbed on Lewis acid sites to form N2 and H2O could be the main reaction pathway,and oxygen adsorption might favor this process.展开更多
A series of Fe‐Mn/Al2O3 catalysts were prepared and studied for low temperature selective catalytic reduction （SCR） of NO with NH3 in a fixed‐bed reactor. The effects of Fe and Mn on NO conversion and the deactiva...A series of Fe‐Mn/Al2O3 catalysts were prepared and studied for low temperature selective catalytic reduction （SCR） of NO with NH3 in a fixed‐bed reactor. The effects of Fe and Mn on NO conversion and the deactivation of the catalysts were studied. N2 adsorption‐desorption, X‐ray diffraction, transmission electron microscopy, energy dispersive spectroscopy, H2 temperature‐programmed reduction, NH3 temperature‐programmed desorption, X‐ray photoelectron spectroscopy （XPS）, thermal gravimetric analysis and Fourier transform infrared spectroscopy were used to character‐ize the catalysts. The 8Fe‐8Mn/Al2O3 catalyst gave 99%of NO conversion at 150？？ and more than 92.6%NO conversion was obtained in a wide low temperature range of 90–210？？. XPS analysis demonstrated that the Fe3＋was the main iron valence state on the catalyst surface and the addition of Mn increased the accumulation of Fe on the surface. The higher specific surface area, enhanced dispersion of amorphous Fe and Mn, improved reduction properties and surface acidity, lower binding energy, higher Mn4＋/Mn3＋ratio and more adsorbed oxygen species resulted in higher NO conversion for the 8Fe‐8Mn/Al2O3 catalyst. In addition, the SCR activity of the 8Fe‐8Mn/Al2O3 cata‐lyst was only slightly decreased in the presence of H2O and SO2, which indicated that the catalyst had better tolerance to H2O and SO2. The reaction temperature was crucial for the SO2 resistance of catalyst and the decrease of catalytic activity caused by SO2 was mainly due to the sulfate salts formed on the catalyst.展开更多
ZSM-5 zeolites were directly synthesized on the surface of honeycomb cordierite substrates by hydrothermal method and certified by XRD and SEM techniques; the adhesion of ZSM-5 coatings was evaluated by ultrasonic vib...ZSM-5 zeolites were directly synthesized on the surface of honeycomb cordierite substrates by hydrothermal method and certified by XRD and SEM techniques; the adhesion of ZSM-5 coatings was evaluated by ultrasonic vibration. Cu-ZSM-5/cordierite monolithic catalyst was prepared by ion-exchange and impregnation method and applied for the selective catalytic reduction （SCR） of NO by NH3 using a simulated diesel exhaust. The results show that the cordierite surface is almost completely covered by ZSM-5 crystals and the crystallization time greatly impacts the loadings and adhesion of ZSM-5 coatings on substrate, the NOx removal rate over Cu-ZSM-5/cordierite is above 90% in a temperature range of 240-480℃. Moreover, Cu-ZSM-5/cordierite prepared by different methods shows a wide temperature window （240-540 ℃） with high NO removal activities.展开更多
Different transition metals were used to modify V2O5-based catalysts （M-V, M = Cu, Fe, Mn, Co） on TiO2 via impregnation, for the selective reduction of NO with NH3. The introduced metals induced high dispersion in t...Different transition metals were used to modify V2O5-based catalysts （M-V, M = Cu, Fe, Mn, Co） on TiO2 via impregnation, for the selective reduction of NO with NH3. The introduced metals induced high dispersion in the vanadium species and the formation of vanadates on the TiO2 support, and increased the amount of surface acid sites and the strength of these acids. The strong acid sites might be responsible for the high N2 selectivity at higher temperatures. Among these catalysts, Cu-V/TiO2 showed the highest activity and N2 selectivity at 225-375 ~C. The results of X-ray photo- electron spectroscopy, NH3-temperature-programmed desorption, and in-situ diffuse reflectance infrared Fourier transform spectroscopy suggested that the improved performance was probably due to more active surface oxygen species and increased strong surface acid sites. The outstanding activity, stability, and SO2/H2O durability of Cu-V/TiO2 make it a candidate to be a NOx removal catalyst for stationary flue gas.展开更多
Fe doped Beta zeolite with different Fe contents were prepared by ion exchange by changing the volume or the concentration of a Fe salt solution. For a particular mass of Fe salt precursor, the concentration of the me...Fe doped Beta zeolite with different Fe contents were prepared by ion exchange by changing the volume or the concentration of a Fe salt solution. For a particular mass of Fe salt precursor, the concentration of the metal salt solution during ion exchange influenced the ion exchange capacity of Fe, and resulted in different activities of the Fe-Beta catalyst. Fe-Beta catalysts with the Fe contents of （2.6, 6.3 and 9） wt% were synthesized using different amounts of 0.02 mol/L Fe salt solution. These catalysts were studied by various characterization techniques and their NH3-SCR activities were evaluated. The Fe-Beta catalyst with the Fe content of 6.3 wt% exhibited the highest activity, with a temperature range of 202-616℃ where the NOx conversion was 〉 80%. The Fe content in Beta zeolite did not influence the structure of Beta zeolite and valence state of Fe. Compared with the Fe-Beta catalysts with low Fe content （2.6 wt%）, Fe-Beta catalysts with 6.3 wt% Fe content possessed more isolated Fe3. active sites which led to its higher NH3-SCR activity. A high capacity for NH3 and NO adsorption, and a high activity for NO oxidation also contributed to the high NH3-SCR activity of the Fe-Beta catalyst with 6.3 wt%. However, when the Fe content was further increased to 9.0 wt%, the amount of FexOy nanoparticles increased while the amount of isolated Fe3＋ active sites was unchanged, which promoted NH3 oxidation and decreased the NH3-SCR activity at high temperature.展开更多
Binary metal oxide（MnOx-A/TiO2）catalysts were prepared by adding the second metal to manganese oxides supported on titanium dioxide（TiO2）,where,A indicates Fe2O3,WO3,MoO3,and Cr2O3.Their catalytic activity,N2 sele...Binary metal oxide（MnOx-A/TiO2）catalysts were prepared by adding the second metal to manganese oxides supported on titanium dioxide（TiO2）,where,A indicates Fe2O3,WO3,MoO3,and Cr2O3.Their catalytic activity,N2 selectivity,and SO2 poisonous tolerance were investigated.The catalytic performance at low temperatures decreased in the following order：Mn-W/TiO2〉Mn-Fe/TiO2〉Mn-Cr/TiO2〉Mn-Mo/TiO2,whereas the N2 selectivity decreased in the order：Mn-Fe/TiO2〉Mn-W/TiO2〉Mn-Mo/TiO2〉Mn-Cr/TiO2.In the presence of 0.01%SO2 and 6%H2O,the NOx conversions in the presence of Mn-W/TiO2,Mn-Fe/TiO2,or Mn-Mo/TiO2 maintain 98.5%,95.8%and 94.2%, respectively,after 8 h at 120°C at GHSV 12600 h？ 1 .As effective promoters,WO3 and Fe2O3 can increase N2 selectivity and the resistance to SO2 of MnOx/TiO2 significantly.The Fourier transform infrared（FTIR）spectra of NH3 over WO3 show the presence of Lewis acid sites.The results suggest that WO3 is the best promoter of MnOx/TiO2,and Mn-W/TiO2 is one of the most active catalysts for the low temperature selective catalytic reduction of NO with NH3.展开更多
The catalytic activities of MnOx-WO3/TiO2 for selective catalytic reduction（SCR） of NO with NH3 were investigated in a wide range of temperature and reaction condition.It yielded a NOx conversion of 80.3%—99.6% and...The catalytic activities of MnOx-WO3/TiO2 for selective catalytic reduction（SCR） of NO with NH3 were investigated in a wide range of temperature and reaction condition.It yielded a NOx conversion of 80.3%—99.6% and a N2 product selectivity of 100%—98.7% during 100 °C to 350 °C at gas hourly space velocity（GHSV）=18900 h-1.In the presence of 0.01% SO2 and 6% H2O at 120 °C,the NOx conversion can maintain 98.5%.At 300 °C and with 0.07% SO2 in reactant stream,the NOx conversion stabilized at 99% as high as the commercial V-W/TiO2 catalyst＇s level.The steady-state kinetics study shows that O2 played a promoting role.In the presence of less than 1.5% O2,NOx conversion can increase sharply with the increase of O2 concentration.The reaction order was zero with respect to NH3 and first with respect to NO with excess O2 and H2O.The kinetics active energy（Ea） of Mn-W/TiO2 was calculated to be 6.24 kJ/mol according to the kinetic experiment at various temperatures,much lower than those of other catalysts reported in the literature.Mn-W/TiO2 is an excellent catalyst for SCR of NO with NH3 by now.展开更多
A series of H3PO4-modified CeO2 samples were prepared by impregnation of CeO2 with H3PO4solution,and evaluated for the selective catalytic reduction of NOx by NH3.The samples were characterized by X-ray diffraction,N2...A series of H3PO4-modified CeO2 samples were prepared by impregnation of CeO2 with H3PO4solution,and evaluated for the selective catalytic reduction of NOx by NH3.The samples were characterized by X-ray diffraction,N2 adsorption-desorption,infrared spectroscopy,Raman spectroscopy,X-ray photoelectron spectroscopy,temperature-programmed desorption of NH3,and temperature-programmed reduction of H2.The results showed that more than 80%NO conversion was achieved in the temperature range 250-550℃ over the H3PO4-CeO2 catalyst.The enhanced catalytic performance could be ascribed to the increase in acidic strength,especially Bronsted acidity,and reduction in redox properties of the CeO2 after H3PO4 modification.展开更多
A titania pillared interlayered clay（Ti-PILC） supported vanadia catalyst（V2O5/TiO2-PILC） was prepared by wet impregnation for the selective catalytic reduction（SCR） of NO with ammonia. Compared to the traditiona...A titania pillared interlayered clay（Ti-PILC） supported vanadia catalyst（V2O5/TiO2-PILC） was prepared by wet impregnation for the selective catalytic reduction（SCR） of NO with ammonia. Compared to the traditional V2O5/TiO2 and V2O5-MoO3/TiO2 catalysts, the V2O5/TiO2-PILC catalyst exhibited a higher activity and better SO2 and H2O resistance in the NH3-SCR reaction. Characterization using TPD, in situ DRIFT and XPS showed that surface sulfate and/or sulfite species and ionic SO4^（2-）species were formed on the catalyst in the presence of SO2. The ionic SO4^（2-） species on the catalyst surface was one reason for deactivation of the catalyst in SCR. The formation of the ionic SO4^（2-） species was correlated with the amount of surface adsorbed oxygen species. Less adsorbed oxygen species gave less ionic SO4^（2-） species on the catalyst.展开更多
We first received the previously unknown pattern of the magnetic field and relativistic effects on chemical reactions in catalysis for example, reduction NO with monooxide carbon with used magnetic uranium catalysts, ...We first received the previously unknown pattern of the magnetic field and relativistic effects on chemical reactions in catalysis for example, reduction NO with monooxide carbon with used magnetic uranium catalysts, which is to reduce the activation energy of the reactants with increasing concentration of magnetic materials and due to the interaction and control of the motion of ions and electrons with atoms and attraction between ions by means of a magnetic field.展开更多
In the present study,we synthesized CeO2 catalysts doped with various transition metals(M=Co,Fe,or Cu)using a supercritical water hydrothermal route,which led to the incorporation of the metal ions in the CeO2 lattice...In the present study,we synthesized CeO2 catalysts doped with various transition metals(M=Co,Fe,or Cu)using a supercritical water hydrothermal route,which led to the incorporation of the metal ions in the CeO2 lattice,forming solid solutions.The catalysts were then used for the selective catalytic reduction(SCR)of NO by CO.The Cu‐doped catalyst exhibited the highest SCR activity;it had a T50(i.e.,50%NO conversion)of only 83°C and a T90(i.e.,90%NO conversion)of 126°C.Such an activity was also higher than in many state‐of‐the‐art catalysts.In situ diffuse reflectance Fourier transform infrared spectroscopy suggested that the MOx‐CeO2 catalysts(M=Co and Fe)mainly followed an Eley‐Rideal reaction mechanism for CO‐SCR.In contrast,a Langmuir‐Hinshelwood SCR reaction mechanism occurred in CuO‐CeO2 owing to the presence of Cu+species,which ensured effective adsorption of CO.This explains why CuO‐CeO2 exhibited the highest activity with regard to the SCR of NO by CO.展开更多
Two series of Mn/beta and Mn/ZSM‐5catalysts were prepared to study the influence of how different Mn precursors,introduced to the respective parent zeolites by wet impregnation,affected the selective catalytic reduct...Two series of Mn/beta and Mn/ZSM‐5catalysts were prepared to study the influence of how different Mn precursors,introduced to the respective parent zeolites by wet impregnation,affected the selective catalytic reduction(SCR)of NO by NH3across a low reaction temperature window of50–350°C.In this study,the catalysts were characterized using N2adsorption/desorption,X‐ray diffraction,X‐ray fluorescence,H2temperature‐programmed reduction,NH3temperature‐programmed desorption and X‐ray photoelectron spectroscopy.As the manganese chloride precursor only partially decomposed this primarily resulted in the formation of MnCl2in addition to the presence of low levels of crystalline Mn3O4,which resulted in poor catalytic performance.However,the manganese nitrate precursor formed crystalline MnO2as the major phase in addition to a minor presence of unconverted Mn‐nitrate.Furthermore,manganese acetate resulted principally in a mixture of amorphous Mn2O3and MnO2,and crystalline Mn3O4.From all the catalysts screened,the test performance data showed Mn/beta‐Ac to exhibit the highest NO conversion(97.5%)at240°C,which remained>90%across a temperature window of220–350°C.The excellent catalytic performance was ascribed to the enrichment of highly dispersed MnOx(Mn2O3and MnO2)species that act as the active phase in the NH3‐SCR process.Furthermore,together with a suitable amount of weakly acidic centers,higher concentration of surface manganese and a greater presence of surface labile oxygen groups,SCR performance was collectively enhanced at low temperature.?2018,Dalian Institute of Chemical Physics,Chinese Academy of Sciences.Published by Elsevier B.V.All rights reserved.展开更多
In this study,a MnOx@TiO2 core‐shell catalyst prepared by a two‐step method was used for the low‐temperature selective catalytic reduction of NOx with NH3.The catalyst exhibits high activity,high stability,and exce...In this study,a MnOx@TiO2 core‐shell catalyst prepared by a two‐step method was used for the low‐temperature selective catalytic reduction of NOx with NH3.The catalyst exhibits high activity,high stability,and excellent N2 selectivity.Furthermore,it displays better SO2 and H2O tolerance than its MnOx,TiO2,and MnOx/TiO2 counterparts.The prepared catalyst was characterized systematically by transmission electron microscopy,high‐resolution transmission electron microscopy,X‐ray diffraction,Raman,BET,X‐ray photoelectron spectroscopy,NH3 temperature‐programmed desorption and H2 temperature‐programmed reduction analyses.The optimized MnOx@TiO2 catalyst exhibits an obvious core‐shell structure,where the TiO2 shell is evenly distributed over the MnOx nanorod core.The catalyst also presents abundant mesopores,Lewis‐acid sites,and high redox capability,all of which enhance its catalytic performance.According to the XPS results,the decrease in the number of Mn4+active centers after SO2 poisoning is significantly lower in MnOx@TiO2 than in MnOx/TiO2.The core‐shell structure is hence able to protect the catalytic active sites from H2O and SO2 poisoning.展开更多
The catalyst of Fe-Mo/ZSM-5 has been found to be more active than Fe-ZSM-5 and Mo/ZSM-5 separately for selective catalytic reduction （SCR） of nitric oxide （NO） with NH3. The kinetics of the SCR reaction in the pre...The catalyst of Fe-Mo/ZSM-5 has been found to be more active than Fe-ZSM-5 and Mo/ZSM-5 separately for selective catalytic reduction （SCR） of nitric oxide （NO） with NH3. The kinetics of the SCR reaction in the presence of O2 was studied in this work. The results showed that the observed reaction orders were 0.74-0.99, 0.01-0.13, and 0 for NO, O2 and NH3 at 350-450℃, respectively. And the apparent activation energy of the SCR was 65 kJ/mol on the Fe-Mo/ZSM-5 catalyst. The SCR mechanism was also deduced. Adsorbed NO species can react directly with adsorbed ammonia species on the active sites to form N2 and H2O. Gaseous O2 might serve as a reoxidizing agent for the active sites that have undergone reduction in the SCR process. It is also important to note that a certain amount of NO was decomposed directly over the Fe-Mo/ZSM-5 catalyst in the absence of NH3.展开更多
Catalytic properties of MnOx-FeOx complex oxide （hereafter denoted as Mn-Fe） catalysts modified with different loadings of chromium oxide were investigated by using the combination of physico-cbemical techniques, su...Catalytic properties of MnOx-FeOx complex oxide （hereafter denoted as Mn-Fe） catalysts modified with different loadings of chromium oxide were investigated by using the combination of physico-cbemical techniques, such as N2 physisorption, X-ray diffraction （XRD）, high-resolution transmission electron microscope （HRTEM）, in situ Fourier transform infrared spectroscopy （in situ FT-IR） and temperature-programmed reduction （TPR） and their catalytic activities were evaluated with the selective catalytic reduction （SCR） of NOx by NH3. It was found that with the addition of Cr, more NO could be removed in the low-temperature window （below 120 ℃）. Among the tested catalysts, Mn-Fe- Cr （2 ： 2 ： 1） catalyst exhibited the best catalytic performance at 80 ℃ with the NO conversion higher than 90%. The combination of the reaction and characterization results indicated that （1） the strong interaction among tertiary metal oxides existed in the catalysts when Cr was appropriately added, which made the active components better dispersed with less agglomeration and sintering and the largest BET specific surface area could be obtained; （2） Cr improved the low-temperature reducibility of the catalyst and promoted the formation of the active intermediate （-NH3＋）, which favored the low-temperature SCR reaction.展开更多
This paper reports observations of significant synergistic effects between dielectric barrier discharge (DBD) plasmas and Cu-ZSM-5 catalysts for C2H4 selective reduction of NOx at 250 °C in the presence of excess...This paper reports observations of significant synergistic effects between dielectric barrier discharge (DBD) plasmas and Cu-ZSM-5 catalysts for C2H4 selective reduction of NOx at 250 °C in the presence of excess oxygen by using a one-stage plasma-over-catalyst (POC) reactor. With the reactant gas mixture of 530 ppm NO, 650 ppm C2H4, 5.8% O2 in N2 and GHSV = 12000 h-1, the pure catalytic, pure plasma-induced (discharges over fused silica pellets) and plasma- catalytic (in the POC reactor) NOx conversion are 39%, 1.5% and 79%, respectively. The in-situ optical emission spectra of the reactive systems imply some short-lived active species formed from plasma-induced and plasma-catalytic processes may be responsible to the observed synergistic effects in this one-stage POC system.展开更多
The low‐temperature hydrothermal stabilities of Cu‐SAPO‐34samples with various Si contents and Cu loadings were systematically investigated.The NH3oxidation activities and NH3‐selective catalytic reduction(SCR)act...The low‐temperature hydrothermal stabilities of Cu‐SAPO‐34samples with various Si contents and Cu loadings were systematically investigated.The NH3oxidation activities and NH3‐selective catalytic reduction(SCR)activities(mainly the low‐temperature activities)of all the Cu‐SAPO‐34catalysts declined after low‐temperature steam treatment(LTST).These results show that the texture and acid density of Cu‐SAPO‐34can be better preserved by increasing the Cu loading,although the hydrolysis of Si-O-Al bonds is inevitable.The stability of Cu ions and the stability of the SAPO framework were positively correlated at relatively low Cu loadings.However,a high Cu loading(e.g.,3.67wt%)resulted in a significant decrease in the number of isolated Cu ions.Aggregation of CuO particles also occurred during the LTST,which accounts for the decreasing NH3oxidation activities of the catalysts.Among the catalysts,Cu‐SAPO‐34with a high Si content and medium Cu content(1.37wt%)showed the lowest decrease in NH3‐SCR because its Cu2+content was well retained and its acid density was well preserved.展开更多
Monolithic catalysts of Pt/La-Al2O3 and Pt/Ce0.67Zr0.3302 were prepared to investigate methane selective catalytic reduction （SCR） of NO. The results indicate that Pt/Ce0.67Zr0.33O2 shows high activity and both NO a...Monolithic catalysts of Pt/La-Al2O3 and Pt/Ce0.67Zr0.3302 were prepared to investigate methane selective catalytic reduction （SCR） of NO. The results indicate that Pt/Ce0.67Zr0.33O2 shows high activity and both NO and CH4 can be converted completely at 450℃. Meanwhile, NO and CH4 can be converted completely when there exists excess oxygen. The Pt/Ce0.67Zr0.33O2 catalyst were further investigated by using methane as reducing agent to SCR NO in a novel equipment which combined the CH4 selective catalytic reduction of NO with methane combustion. The result shows that the catalyst is high active and the novel equipment is very effective. The conversion of NO is above 92% under the conditions used in this work. The prepared burner and catalysts have great potential for application.展开更多
The V/O5-WO3-MoOy＇TiO2 honeycomb catalyst was prepared with industrial grade chemicals. The structural and physico-chemical properties were analyzed with X-ray diffraction （XRD）, scanning electron micrograph （SEM...The V/O5-WO3-MoOy＇TiO2 honeycomb catalyst was prepared with industrial grade chemicals. The structural and physico-chemical properties were analyzed with X-ray diffraction （XRD）, scanning electron micrograph （SEM） and mercury porosimetry. The NOx conversion and durability were investigated on a pilot plant test set under the actual operational conditions of a coal fired boiler. The catalyst monolith had good formability with mass per- centage of V ： W ： Mo ： TiO2 ： fiber glass = 1 ： 4.5 ： 4.5 ： 72 ： 18. Vanadium, tungsten and molybdenum species were highly dispersed on anatase TiO2 without causing the transformation of anatase TiO2 to ruffle by calcining under a current of air at 450℃ for 4.5 h, but there were some degrees of crystal distortion. The catalyst particle sizes were almost uniform with close pile-up and the pore structure was regular with complete macro-pore formation and large specific surface area. The NOx conversion was sensitive to temperature but nearly insensitive to NH3. The catalyst showed strong adaptability to NOx concentration with activity above 80% in the range of 615 1640 mg.m-3. Within the range of 720-8640 h continuous operation, the NOx conversion dropped at a rate of about 1% reduction per 600 h.展开更多
基金supported by the Bureau of Science and Technology,Fujian Province,China(2015H0043)the Strategic Priority Research Program of the Chinese Academy of Sciences(XDB05050500)the National Natural Science Foundation of China(21403210)~~
文摘A series of CuSO4/TiO2 catalysts were prepared using a wet impregnation method.The activity of each sample in the selective catalytic reduction of NO by NH3（NH3-SCR） was determined.The effects of SO2 and H2O,and their combined effect,on the activity were examined at 340 ℃ for 24 h.The catalysts were characterized using N2 adsorption-desorption,X-ray diffraction,X-ray photoelectron spectroscopy,temperature-programmed reduction of H2（H2-TPR）,temperature-programmed desorption of NH3（NH3-TPD）,and in situ diffuse-reflectance infrared Fourier-transform spectroscopy（DRIFTS）.The CuSO4/TiO2 catalysts had good activities,with low production of N2O above 340 ℃.SO2 or a combination of SO2 and H2O had little effect on the activity,and H2O caused only a slight decrease in activity during the experimental period.The NH3-TPD and H2-TPR results showed that CuSO4 increased the amounts of acid sites and adsorbed oxygen on the catalyst.In situ DRIFTS showed that the NH3-SCR reaction on the CuSO4/TiO2 catalysts followed an Eley-Rideal mechanism.The reaction of gaseous NO with NH3 adsorbed on Lewis acid sites to form N2 and H2O could be the main reaction pathway,and oxygen adsorption might favor this process.
基金supported by the National High Technology Research and Development Program of China (863 Program,2015AA03A401)the National Natural Science Foundation of China (51276039)+1 种基金the Fundamental Research Funds for the Central Universities (020514380020,020514380030)the Postdoctoral Science Foundation of Jiangsu Province,China (1501033A)~~
文摘A series of Fe‐Mn/Al2O3 catalysts were prepared and studied for low temperature selective catalytic reduction （SCR） of NO with NH3 in a fixed‐bed reactor. The effects of Fe and Mn on NO conversion and the deactivation of the catalysts were studied. N2 adsorption‐desorption, X‐ray diffraction, transmission electron microscopy, energy dispersive spectroscopy, H2 temperature‐programmed reduction, NH3 temperature‐programmed desorption, X‐ray photoelectron spectroscopy （XPS）, thermal gravimetric analysis and Fourier transform infrared spectroscopy were used to character‐ize the catalysts. The 8Fe‐8Mn/Al2O3 catalyst gave 99%of NO conversion at 150？？ and more than 92.6%NO conversion was obtained in a wide low temperature range of 90–210？？. XPS analysis demonstrated that the Fe3＋was the main iron valence state on the catalyst surface and the addition of Mn increased the accumulation of Fe on the surface. The higher specific surface area, enhanced dispersion of amorphous Fe and Mn, improved reduction properties and surface acidity, lower binding energy, higher Mn4＋/Mn3＋ratio and more adsorbed oxygen species resulted in higher NO conversion for the 8Fe‐8Mn/Al2O3 catalyst. In addition, the SCR activity of the 8Fe‐8Mn/Al2O3 cata‐lyst was only slightly decreased in the presence of H2O and SO2, which indicated that the catalyst had better tolerance to H2O and SO2. The reaction temperature was crucial for the SO2 resistance of catalyst and the decrease of catalytic activity caused by SO2 was mainly due to the sulfate salts formed on the catalyst.
基金Project (20906067) supported by the National Natural Science Foundation of China
文摘ZSM-5 zeolites were directly synthesized on the surface of honeycomb cordierite substrates by hydrothermal method and certified by XRD and SEM techniques; the adhesion of ZSM-5 coatings was evaluated by ultrasonic vibration. Cu-ZSM-5/cordierite monolithic catalyst was prepared by ion-exchange and impregnation method and applied for the selective catalytic reduction （SCR） of NO by NH3 using a simulated diesel exhaust. The results show that the cordierite surface is almost completely covered by ZSM-5 crystals and the crystallization time greatly impacts the loadings and adhesion of ZSM-5 coatings on substrate, the NOx removal rate over Cu-ZSM-5/cordierite is above 90% in a temperature range of 240-480℃. Moreover, Cu-ZSM-5/cordierite prepared by different methods shows a wide temperature window （240-540 ℃） with high NO removal activities.
基金supported by the National Natural Science Foundation of China (21303099)the National Basic Research Program of China(973 Program,2014CB660803)+1 种基金the Shanghai Municipal Education Commission(14ZZ097, B.3704713001)the Research Fund for Innovation Program of Shanghai University (K.10040713003)~~
文摘Different transition metals were used to modify V2O5-based catalysts （M-V, M = Cu, Fe, Mn, Co） on TiO2 via impregnation, for the selective reduction of NO with NH3. The introduced metals induced high dispersion in the vanadium species and the formation of vanadates on the TiO2 support, and increased the amount of surface acid sites and the strength of these acids. The strong acid sites might be responsible for the high N2 selectivity at higher temperatures. Among these catalysts, Cu-V/TiO2 showed the highest activity and N2 selectivity at 225-375 ~C. The results of X-ray photo- electron spectroscopy, NH3-temperature-programmed desorption, and in-situ diffuse reflectance infrared Fourier transform spectroscopy suggested that the improved performance was probably due to more active surface oxygen species and increased strong surface acid sites. The outstanding activity, stability, and SO2/H2O durability of Cu-V/TiO2 make it a candidate to be a NOx removal catalyst for stationary flue gas.
基金supported by the National Key Basic Research Program of China (973 Program, 2013CB933201)the National Natural Science Foun-dation of China (21577034, 21333003, 91545103)+1 种基金Science and Technology Commission of Shanghai Municipality (16ZR1407900)Fundamental Research Funds for the Central Universities (WJ1514020)~~
文摘Fe doped Beta zeolite with different Fe contents were prepared by ion exchange by changing the volume or the concentration of a Fe salt solution. For a particular mass of Fe salt precursor, the concentration of the metal salt solution during ion exchange influenced the ion exchange capacity of Fe, and resulted in different activities of the Fe-Beta catalyst. Fe-Beta catalysts with the Fe contents of （2.6, 6.3 and 9） wt% were synthesized using different amounts of 0.02 mol/L Fe salt solution. These catalysts were studied by various characterization techniques and their NH3-SCR activities were evaluated. The Fe-Beta catalyst with the Fe content of 6.3 wt% exhibited the highest activity, with a temperature range of 202-616℃ where the NOx conversion was 〉 80%. The Fe content in Beta zeolite did not influence the structure of Beta zeolite and valence state of Fe. Compared with the Fe-Beta catalysts with low Fe content （2.6 wt%）, Fe-Beta catalysts with 6.3 wt% Fe content possessed more isolated Fe3. active sites which led to its higher NH3-SCR activity. A high capacity for NH3 and NO adsorption, and a high activity for NO oxidation also contributed to the high NH3-SCR activity of the Fe-Beta catalyst with 6.3 wt%. However, when the Fe content was further increased to 9.0 wt%, the amount of FexOy nanoparticles increased while the amount of isolated Fe3＋ active sites was unchanged, which promoted NH3 oxidation and decreased the NH3-SCR activity at high temperature.
文摘Binary metal oxide（MnOx-A/TiO2）catalysts were prepared by adding the second metal to manganese oxides supported on titanium dioxide（TiO2）,where,A indicates Fe2O3,WO3,MoO3,and Cr2O3.Their catalytic activity,N2 selectivity,and SO2 poisonous tolerance were investigated.The catalytic performance at low temperatures decreased in the following order：Mn-W/TiO2〉Mn-Fe/TiO2〉Mn-Cr/TiO2〉Mn-Mo/TiO2,whereas the N2 selectivity decreased in the order：Mn-Fe/TiO2〉Mn-W/TiO2〉Mn-Mo/TiO2〉Mn-Cr/TiO2.In the presence of 0.01%SO2 and 6%H2O,the NOx conversions in the presence of Mn-W/TiO2,Mn-Fe/TiO2,or Mn-Mo/TiO2 maintain 98.5%,95.8%and 94.2%, respectively,after 8 h at 120°C at GHSV 12600 h？ 1 .As effective promoters,WO3 and Fe2O3 can increase N2 selectivity and the resistance to SO2 of MnOx/TiO2 significantly.The Fourier transform infrared（FTIR）spectra of NH3 over WO3 show the presence of Lewis acid sites.The results suggest that WO3 is the best promoter of MnOx/TiO2,and Mn-W/TiO2 is one of the most active catalysts for the low temperature selective catalytic reduction of NO with NH3.
文摘The catalytic activities of MnOx-WO3/TiO2 for selective catalytic reduction（SCR） of NO with NH3 were investigated in a wide range of temperature and reaction condition.It yielded a NOx conversion of 80.3%—99.6% and a N2 product selectivity of 100%—98.7% during 100 °C to 350 °C at gas hourly space velocity（GHSV）=18900 h-1.In the presence of 0.01% SO2 and 6% H2O at 120 °C,the NOx conversion can maintain 98.5%.At 300 °C and with 0.07% SO2 in reactant stream,the NOx conversion stabilized at 99% as high as the commercial V-W/TiO2 catalyst＇s level.The steady-state kinetics study shows that O2 played a promoting role.In the presence of less than 1.5% O2,NOx conversion can increase sharply with the increase of O2 concentration.The reaction order was zero with respect to NH3 and first with respect to NO with excess O2 and H2O.The kinetics active energy（Ea） of Mn-W/TiO2 was calculated to be 6.24 kJ/mol according to the kinetic experiment at various temperatures,much lower than those of other catalysts reported in the literature.Mn-W/TiO2 is an excellent catalyst for SCR of NO with NH3 by now.
基金supported by the National Natural Science Foundation of China(21177120)the Open Fund of Key Laboratory of Functional Inorganic Material Chemistry(Heilongjiang University),Ministry of Education~~
文摘A series of H3PO4-modified CeO2 samples were prepared by impregnation of CeO2 with H3PO4solution,and evaluated for the selective catalytic reduction of NOx by NH3.The samples were characterized by X-ray diffraction,N2 adsorption-desorption,infrared spectroscopy,Raman spectroscopy,X-ray photoelectron spectroscopy,temperature-programmed desorption of NH3,and temperature-programmed reduction of H2.The results showed that more than 80%NO conversion was achieved in the temperature range 250-550℃ over the H3PO4-CeO2 catalyst.The enhanced catalytic performance could be ascribed to the increase in acidic strength,especially Bronsted acidity,and reduction in redox properties of the CeO2 after H3PO4 modification.
基金supported by the National Natural Science Foundation of China(21277009,21577005)~~
文摘A titania pillared interlayered clay（Ti-PILC） supported vanadia catalyst（V2O5/TiO2-PILC） was prepared by wet impregnation for the selective catalytic reduction（SCR） of NO with ammonia. Compared to the traditional V2O5/TiO2 and V2O5-MoO3/TiO2 catalysts, the V2O5/TiO2-PILC catalyst exhibited a higher activity and better SO2 and H2O resistance in the NH3-SCR reaction. Characterization using TPD, in situ DRIFT and XPS showed that surface sulfate and/or sulfite species and ionic SO4^（2-）species were formed on the catalyst in the presence of SO2. The ionic SO4^（2-） species on the catalyst surface was one reason for deactivation of the catalyst in SCR. The formation of the ionic SO4^（2-） species was correlated with the amount of surface adsorbed oxygen species. Less adsorbed oxygen species gave less ionic SO4^（2-） species on the catalyst.
文摘We first received the previously unknown pattern of the magnetic field and relativistic effects on chemical reactions in catalysis for example, reduction NO with monooxide carbon with used magnetic uranium catalysts, which is to reduce the activation energy of the reactants with increasing concentration of magnetic materials and due to the interaction and control of the motion of ions and electrons with atoms and attraction between ions by means of a magnetic field.
文摘In the present study,we synthesized CeO2 catalysts doped with various transition metals(M=Co,Fe,or Cu)using a supercritical water hydrothermal route,which led to the incorporation of the metal ions in the CeO2 lattice,forming solid solutions.The catalysts were then used for the selective catalytic reduction(SCR)of NO by CO.The Cu‐doped catalyst exhibited the highest SCR activity;it had a T50(i.e.,50%NO conversion)of only 83°C and a T90(i.e.,90%NO conversion)of 126°C.Such an activity was also higher than in many state‐of‐the‐art catalysts.In situ diffuse reflectance Fourier transform infrared spectroscopy suggested that the MOx‐CeO2 catalysts(M=Co and Fe)mainly followed an Eley‐Rideal reaction mechanism for CO‐SCR.In contrast,a Langmuir‐Hinshelwood SCR reaction mechanism occurred in CuO‐CeO2 owing to the presence of Cu+species,which ensured effective adsorption of CO.This explains why CuO‐CeO2 exhibited the highest activity with regard to the SCR of NO by CO.
基金supported by the National Science and Technology Program of China(CDGC01-KT16)~~
文摘Two series of Mn/beta and Mn/ZSM‐5catalysts were prepared to study the influence of how different Mn precursors,introduced to the respective parent zeolites by wet impregnation,affected the selective catalytic reduction(SCR)of NO by NH3across a low reaction temperature window of50–350°C.In this study,the catalysts were characterized using N2adsorption/desorption,X‐ray diffraction,X‐ray fluorescence,H2temperature‐programmed reduction,NH3temperature‐programmed desorption and X‐ray photoelectron spectroscopy.As the manganese chloride precursor only partially decomposed this primarily resulted in the formation of MnCl2in addition to the presence of low levels of crystalline Mn3O4,which resulted in poor catalytic performance.However,the manganese nitrate precursor formed crystalline MnO2as the major phase in addition to a minor presence of unconverted Mn‐nitrate.Furthermore,manganese acetate resulted principally in a mixture of amorphous Mn2O3and MnO2,and crystalline Mn3O4.From all the catalysts screened,the test performance data showed Mn/beta‐Ac to exhibit the highest NO conversion(97.5%)at240°C,which remained>90%across a temperature window of220–350°C.The excellent catalytic performance was ascribed to the enrichment of highly dispersed MnOx(Mn2O3and MnO2)species that act as the active phase in the NH3‐SCR process.Furthermore,together with a suitable amount of weakly acidic centers,higher concentration of surface manganese and a greater presence of surface labile oxygen groups,SCR performance was collectively enhanced at low temperature.?2018,Dalian Institute of Chemical Physics,Chinese Academy of Sciences.Published by Elsevier B.V.All rights reserved.
文摘In this study,a MnOx@TiO2 core‐shell catalyst prepared by a two‐step method was used for the low‐temperature selective catalytic reduction of NOx with NH3.The catalyst exhibits high activity,high stability,and excellent N2 selectivity.Furthermore,it displays better SO2 and H2O tolerance than its MnOx,TiO2,and MnOx/TiO2 counterparts.The prepared catalyst was characterized systematically by transmission electron microscopy,high‐resolution transmission electron microscopy,X‐ray diffraction,Raman,BET,X‐ray photoelectron spectroscopy,NH3 temperature‐programmed desorption and H2 temperature‐programmed reduction analyses.The optimized MnOx@TiO2 catalyst exhibits an obvious core‐shell structure,where the TiO2 shell is evenly distributed over the MnOx nanorod core.The catalyst also presents abundant mesopores,Lewis‐acid sites,and high redox capability,all of which enhance its catalytic performance.According to the XPS results,the decrease in the number of Mn4+active centers after SO2 poisoning is significantly lower in MnOx@TiO2 than in MnOx/TiO2.The core‐shell structure is hence able to protect the catalytic active sites from H2O and SO2 poisoning.
基金Project supported by the CCSS of Shanxi Provincial Government of China(No.200032,200516)
文摘The catalyst of Fe-Mo/ZSM-5 has been found to be more active than Fe-ZSM-5 and Mo/ZSM-5 separately for selective catalytic reduction （SCR） of nitric oxide （NO） with NH3. The kinetics of the SCR reaction in the presence of O2 was studied in this work. The results showed that the observed reaction orders were 0.74-0.99, 0.01-0.13, and 0 for NO, O2 and NH3 at 350-450℃, respectively. And the apparent activation energy of the SCR was 65 kJ/mol on the Fe-Mo/ZSM-5 catalyst. The SCR mechanism was also deduced. Adsorbed NO species can react directly with adsorbed ammonia species on the active sites to form N2 and H2O. Gaseous O2 might serve as a reoxidizing agent for the active sites that have undergone reduction in the SCR process. It is also important to note that a certain amount of NO was decomposed directly over the Fe-Mo/ZSM-5 catalyst in the absence of NH3.
基金supported by Jiangsu Natural Science Foundation (No. BK2012347)the National High Technology and Development Program of China (863 Programs, No.2007AA061802)
文摘Catalytic properties of MnOx-FeOx complex oxide （hereafter denoted as Mn-Fe） catalysts modified with different loadings of chromium oxide were investigated by using the combination of physico-cbemical techniques, such as N2 physisorption, X-ray diffraction （XRD）, high-resolution transmission electron microscope （HRTEM）, in situ Fourier transform infrared spectroscopy （in situ FT-IR） and temperature-programmed reduction （TPR） and their catalytic activities were evaluated with the selective catalytic reduction （SCR） of NOx by NH3. It was found that with the addition of Cr, more NO could be removed in the low-temperature window （below 120 ℃）. Among the tested catalysts, Mn-Fe- Cr （2 ： 2 ： 1） catalyst exhibited the best catalytic performance at 80 ℃ with the NO conversion higher than 90%. The combination of the reaction and characterization results indicated that （1） the strong interaction among tertiary metal oxides existed in the catalysts when Cr was appropriately added, which made the active components better dispersed with less agglomeration and sintering and the largest BET specific surface area could be obtained; （2） Cr improved the low-temperature reducibility of the catalyst and promoted the formation of the active intermediate （-NH3＋）, which favored the low-temperature SCR reaction.
基金supported by the National Natural Science Foundation of China(Grant No.20077005)the National High Technology Research and Development Program("863 Programm”)of China(Grant No.2002AA649140)the Provincial Grants of Science and Technology of Liaoning,China(No.20022112).
文摘This paper reports observations of significant synergistic effects between dielectric barrier discharge (DBD) plasmas and Cu-ZSM-5 catalysts for C2H4 selective reduction of NOx at 250 °C in the presence of excess oxygen by using a one-stage plasma-over-catalyst (POC) reactor. With the reactant gas mixture of 530 ppm NO, 650 ppm C2H4, 5.8% O2 in N2 and GHSV = 12000 h-1, the pure catalytic, pure plasma-induced (discharges over fused silica pellets) and plasma- catalytic (in the POC reactor) NOx conversion are 39%, 1.5% and 79%, respectively. The in-situ optical emission spectra of the reactive systems imply some short-lived active species formed from plasma-induced and plasma-catalytic processes may be responsible to the observed synergistic effects in this one-stage POC system.
基金supported by the National Natural Science Foundation of China(21676262,21506207,21606221)the Key Research Program of Frontier Sciences,CAS(QYZDB-SSW-JSC040)~~
文摘The low‐temperature hydrothermal stabilities of Cu‐SAPO‐34samples with various Si contents and Cu loadings were systematically investigated.The NH3oxidation activities and NH3‐selective catalytic reduction(SCR)activities(mainly the low‐temperature activities)of all the Cu‐SAPO‐34catalysts declined after low‐temperature steam treatment(LTST).These results show that the texture and acid density of Cu‐SAPO‐34can be better preserved by increasing the Cu loading,although the hydrolysis of Si-O-Al bonds is inevitable.The stability of Cu ions and the stability of the SAPO framework were positively correlated at relatively low Cu loadings.However,a high Cu loading(e.g.,3.67wt%)resulted in a significant decrease in the number of isolated Cu ions.Aggregation of CuO particles also occurred during the LTST,which accounts for the decreasing NH3oxidation activities of the catalysts.Among the catalysts,Cu‐SAPO‐34with a high Si content and medium Cu content(1.37wt%)showed the lowest decrease in NH3‐SCR because its Cu2+content was well retained and its acid density was well preserved.
基金Supported by the National High Technology Research and Development Program of China (863 Program, 2006AA06Z347)the NationalNatural Science Foundation of China (20773090).
文摘Monolithic catalysts of Pt/La-Al2O3 and Pt/Ce0.67Zr0.3302 were prepared to investigate methane selective catalytic reduction （SCR） of NO. The results indicate that Pt/Ce0.67Zr0.33O2 shows high activity and both NO and CH4 can be converted completely at 450℃. Meanwhile, NO and CH4 can be converted completely when there exists excess oxygen. The Pt/Ce0.67Zr0.33O2 catalyst were further investigated by using methane as reducing agent to SCR NO in a novel equipment which combined the CH4 selective catalytic reduction of NO with methane combustion. The result shows that the catalyst is high active and the novel equipment is very effective. The conversion of NO is above 92% under the conditions used in this work. The prepared burner and catalysts have great potential for application.
基金Supported by the Science and Technology Development Planning of Shandong Province(2011GSF11716)China Scholarship Council for Researching in University of Birmingham
文摘The V/O5-WO3-MoOy＇TiO2 honeycomb catalyst was prepared with industrial grade chemicals. The structural and physico-chemical properties were analyzed with X-ray diffraction （XRD）, scanning electron micrograph （SEM） and mercury porosimetry. The NOx conversion and durability were investigated on a pilot plant test set under the actual operational conditions of a coal fired boiler. The catalyst monolith had good formability with mass per- centage of V ： W ： Mo ： TiO2 ： fiber glass = 1 ： 4.5 ： 4.5 ： 72 ： 18. Vanadium, tungsten and molybdenum species were highly dispersed on anatase TiO2 without causing the transformation of anatase TiO2 to ruffle by calcining under a current of air at 450℃ for 4.5 h, but there were some degrees of crystal distortion. The catalyst particle sizes were almost uniform with close pile-up and the pore structure was regular with complete macro-pore formation and large specific surface area. The NOx conversion was sensitive to temperature but nearly insensitive to NH3. The catalyst showed strong adaptability to NOx concentration with activity above 80% in the range of 615 1640 mg.m-3. Within the range of 720-8640 h continuous operation, the NOx conversion dropped at a rate of about 1% reduction per 600 h.