The hot deformation simulation of a ZK60 magnesiuln alloy at different temperatures from 373 to 673 K and different strain rates of 0.1, 0.01 and 0.002 s^-1 was studied by using the Gleebe-1500 simulator. The plastic ...The hot deformation simulation of a ZK60 magnesiuln alloy at different temperatures from 373 to 673 K and different strain rates of 0.1, 0.01 and 0.002 s^-1 was studied by using the Gleebe-1500 simulator. The plastic deformation behavior was measured and the deformation activation energy was calculated. The microstructures of ZK60 magnesium alloy with an addition of neodymium during the deformation process were observed by using Polyvar-MET optical microscope and Tecnai G^2 20 TEM. The results show that the working hardening, the dynamic recovery and the dynamic recrystallization occur during the plastic deformation process at different temperatures and strain rates. The dynamic recrystallization starts when the temperature is over 473 K and the DRX grain size after hot deformation is only 5-10 μm. So the refined grains improve both the tensile strength and the elongation of alloys at room temperature. Neodymium is added into the alloy and a precipitate phase Mg12Nd that impedes the movement of dislocations is formed, which benefits to increasing mechanical properties of ZK60 magnesium alloy.展开更多
To investigate the influence of magnitude and distribution of the transverse normal pressure on deformation behavior of sheet metal,viscous pressure bulge test (VPB) of overlapping sheet metals is proposed,where the o...To investigate the influence of magnitude and distribution of the transverse normal pressure on deformation behavior of sheet metal,viscous pressure bulge test (VPB) of overlapping sheet metals is proposed,where the overlapped sheet metal is deformed under the dual-sided normal pressure provided by viscous medium and the overlapping sheet.The transverse normal pressure loading features provided by overlapping sheet metals are first simulated by DEFORM-2D.It shows that the magnitude and space distribution of transverse normal pressure are dependent on strain hardening exponent n-,strength coefficient K-and thickness t-values of the overlapping sheet metal.Based on the stress,deviator stress and strain distribution resulted from the finite element simulation,it indicated that the uniform transverse normal pressure has no effect on deviator stress,the figure and strain distribution of bulge specimens have no change.The non-uniform transverse normal pressure can remarkably change the figure and metal flow of specimens,and the formability of sheet metal can be improved by controlling the transverse normal pressure distribution.展开更多
The Chinese Materials Research Society（C-MRS）Conference（2015）was held in the Guizhou Park Hotel International Conference Center,Guiyang,China,from July 10-14,2015.This conference consists of 30symposia,including 4...The Chinese Materials Research Society（C-MRS）Conference（2015）was held in the Guizhou Park Hotel International Conference Center,Guiyang,China,from July 10-14,2015.This conference consists of 30symposia,including 4international symposia.As one of 4international symposia,＂Serration and noise behavior in advanced materials＂展开更多
China has been developed into one of the most active regions in terms of both fundamental and applied research on magnesium （Mg） and its alloys in the world from a solid base laid by its prominent metallurgist and m...China has been developed into one of the most active regions in terms of both fundamental and applied research on magnesium （Mg） and its alloys in the world from a solid base laid by its prominent metallurgist and materials scientists over the past decades. Nowadays, a large number of young-generation researchers have been inspired by their predecessors and become the key participants in the fields of Mg alloys, which consequently led to the establishment of China Youth Scholar Society for Magnesium Alloys Research in 2015. Since then, the first two China Youth Scholars Symposiums on Mg Alloys Research had been held at Harbin （2015） and Chongqing （2016） China, respectively. A number of crucial research inter- ests related to fundamental and applied Mg research were discussed at the conferences and summarized in this short perspective, aiming to boost far-reaching initiatives for development of new Mg-based materials to satisfy the requirements for a broad range of industrial employments. Herein, four main aspects are included as follows： i） Plastic deformation mechanism and strengthening strategy, ii） Design and development of new Mg-based materials, iii） Key service properties, and iv） New processing technologies.展开更多
基金Project(2006BAE04B02-3)supported by the National Key Program of 11th Five-Year Plan of China
文摘The hot deformation simulation of a ZK60 magnesiuln alloy at different temperatures from 373 to 673 K and different strain rates of 0.1, 0.01 and 0.002 s^-1 was studied by using the Gleebe-1500 simulator. The plastic deformation behavior was measured and the deformation activation energy was calculated. The microstructures of ZK60 magnesium alloy with an addition of neodymium during the deformation process were observed by using Polyvar-MET optical microscope and Tecnai G^2 20 TEM. The results show that the working hardening, the dynamic recovery and the dynamic recrystallization occur during the plastic deformation process at different temperatures and strain rates. The dynamic recrystallization starts when the temperature is over 473 K and the DRX grain size after hot deformation is only 5-10 μm. So the refined grains improve both the tensile strength and the elongation of alloys at room temperature. Neodymium is added into the alloy and a precipitate phase Mg12Nd that impedes the movement of dislocations is formed, which benefits to increasing mechanical properties of ZK60 magnesium alloy.
文摘To investigate the influence of magnitude and distribution of the transverse normal pressure on deformation behavior of sheet metal,viscous pressure bulge test (VPB) of overlapping sheet metals is proposed,where the overlapped sheet metal is deformed under the dual-sided normal pressure provided by viscous medium and the overlapping sheet.The transverse normal pressure loading features provided by overlapping sheet metals are first simulated by DEFORM-2D.It shows that the magnitude and space distribution of transverse normal pressure are dependent on strain hardening exponent n-,strength coefficient K-and thickness t-values of the overlapping sheet metal.Based on the stress,deviator stress and strain distribution resulted from the finite element simulation,it indicated that the uniform transverse normal pressure has no effect on deviator stress,the figure and strain distribution of bulge specimens have no change.The non-uniform transverse normal pressure can remarkably change the figure and metal flow of specimens,and the formability of sheet metal can be improved by controlling the transverse normal pressure distribution.
文摘The Chinese Materials Research Society（C-MRS）Conference（2015）was held in the Guizhou Park Hotel International Conference Center,Guiyang,China,from July 10-14,2015.This conference consists of 30symposia,including 4international symposia.As one of 4international symposia,＂Serration and noise behavior in advanced materials＂
基金support from Chinese Committee for Magnesium and its Application
文摘China has been developed into one of the most active regions in terms of both fundamental and applied research on magnesium （Mg） and its alloys in the world from a solid base laid by its prominent metallurgist and materials scientists over the past decades. Nowadays, a large number of young-generation researchers have been inspired by their predecessors and become the key participants in the fields of Mg alloys, which consequently led to the establishment of China Youth Scholar Society for Magnesium Alloys Research in 2015. Since then, the first two China Youth Scholars Symposiums on Mg Alloys Research had been held at Harbin （2015） and Chongqing （2016） China, respectively. A number of crucial research inter- ests related to fundamental and applied Mg research were discussed at the conferences and summarized in this short perspective, aiming to boost far-reaching initiatives for development of new Mg-based materials to satisfy the requirements for a broad range of industrial employments. Herein, four main aspects are included as follows： i） Plastic deformation mechanism and strengthening strategy, ii） Design and development of new Mg-based materials, iii） Key service properties, and iv） New processing technologies.