The self-developed taper barrel rheomoulding (TBR) machine for light alloy semi-solid slurry preparation was introduced.The semi-solid slurry was obtained from the intense shearing turbulence of the alloy melt in the ...The self-developed taper barrel rheomoulding (TBR) machine for light alloy semi-solid slurry preparation was introduced.The semi-solid slurry was obtained from the intense shearing turbulence of the alloy melt in the cause of solidification, which was further caused by the relative rotation of the internal and external taper barrel whose surface contained wale and groove.The heat transmission model of TBR process, the flow rules and the shearing model of the alloy melt were deduced.Taking A365 as experimental material, the microstructure evolution rules under different slurry preparation processes were analyzed.The results show that decreasing the pouring temperature of A365 alloy melt properly or increasing the shearing rate helps to obtain ideal semi-solid microstructure with the primary particle size of about 70 μm and the shape factor of above 0.8.展开更多
Combat vehicles using armour grade quenched and tempered （Q＆T） steel are needed to be operated under different climatic conditions. However, the properties meeting the room temperature test conditions may not neces...Combat vehicles using armour grade quenched and tempered （Q＆T） steel are needed to be operated under different climatic conditions. However, the properties meeting the room temperature test conditions may not neces-sarily be required to meet the low temperature operating conditions. The influences of shielded metal arc welding （SMAW） process, flux cored arc welding （FCAW） processes and test temperatures below room temperature up to 60℃ on tensile and impact toughness properties of armour grade Q＆T steel welds were reported. The tensile and impact properties of the joints showed incremental trend with respect to the decrement in test temperature up to -40℃ irrespective of the welding processes used. The increment in tensile and impact properties of SMAW and FCAW joints subjected to the low temperature environment is due to plastic strain-induced phase transformation of retained austenite into martensite phase. Among the two processes, SMAW process welded joint showed better tensile and impact properties than its FCAW counterpart joints.展开更多
基金Project(2006CB605203) supported by the National Basic Research Program of China
文摘The self-developed taper barrel rheomoulding (TBR) machine for light alloy semi-solid slurry preparation was introduced.The semi-solid slurry was obtained from the intense shearing turbulence of the alloy melt in the cause of solidification, which was further caused by the relative rotation of the internal and external taper barrel whose surface contained wale and groove.The heat transmission model of TBR process, the flow rules and the shearing model of the alloy melt were deduced.Taking A365 as experimental material, the microstructure evolution rules under different slurry preparation processes were analyzed.The results show that decreasing the pouring temperature of A365 alloy melt properly or increasing the shearing rate helps to obtain ideal semi-solid microstructure with the primary particle size of about 70 μm and the shape factor of above 0.8.
基金the Armament Research Board(ARMREB),Directorate of Armaments,Ministry of Defense,New Delhi,Government of India for providing financial support to carry out this investigation through a CARS project,No.CVRDE/MMG/2011-2012/003/CARS dated 23rd May 2011
文摘Combat vehicles using armour grade quenched and tempered （Q＆T） steel are needed to be operated under different climatic conditions. However, the properties meeting the room temperature test conditions may not neces-sarily be required to meet the low temperature operating conditions. The influences of shielded metal arc welding （SMAW） process, flux cored arc welding （FCAW） processes and test temperatures below room temperature up to 60℃ on tensile and impact toughness properties of armour grade Q＆T steel welds were reported. The tensile and impact properties of the joints showed incremental trend with respect to the decrement in test temperature up to -40℃ irrespective of the welding processes used. The increment in tensile and impact properties of SMAW and FCAW joints subjected to the low temperature environment is due to plastic strain-induced phase transformation of retained austenite into martensite phase. Among the two processes, SMAW process welded joint showed better tensile and impact properties than its FCAW counterpart joints.