The effects of rare earths(RE)-Mg-Ti compound modification on the structures and properties of high-carbon high speed steel(HSS) were researched.The impact toughness(α_k),the fracture toughness(K_(1c))and threshold o...The effects of rare earths(RE)-Mg-Ti compound modification on the structures and properties of high-carbon high speed steel(HSS) were researched.The impact toughness(α_k),the fracture toughness(K_(1c))and threshold of fatigue crack growth(ΔK_(th))are tested.The thermal fatigue test is done on a self-straining thermal fatigue tester,the wear test is done on a high temperature wear test machine.The results show that the matrix can be refined by the RE-Mg-Ti compound modification,the eutectic carbides are inclined to spheroidicize and are distributed evenly,the morphology and distribution of eutectic carbides are improved by appropriate RE-Mg-Ti complex modification.After RE-Mg-Ti compound modification,a little effects can be found on the strength,hardness and red hardness,but the fracture toughness(K_(1c)) and threshold of fatigue crack growth(△K_(th)) are improved in the meantime,the impact toughness (α_k) is increased by over one time,and the resistance to thermal fatigue and wear resistance at an elevated temperature are remarkably improved.展开更多
A new hot-work die steel for hot stamping was developed, and used the die for mass production. The produced die showed good performance owing to its high heat conductivity and wear-resistant characteristics. Two diffe...A new hot-work die steel for hot stamping was developed, and used the die for mass production. The produced die showed good performance owing to its high heat conductivity and wear-resistant characteristics. Two different benchmarking hot-work die steels were investigated, and then compared in terms of their impact ductility, temper characteristics ,heat conductivity, and thermal stability. The result of the high-temperature friction wear test indicated that oxidative wear was the main mode in high temperature. On the basis of the comparison and test results, the alloying composition of the new hot-work die steel was especially designed. The new die steel showed good performance with good wear-resistant quality, as well as temper hardness and heat conductivity of HRC 50 and 34.3 W/（ m ~ K）, respectively. Furthermore, without surface plasma nitriding, the die made of the new steel had no obvious galling with 6 142 strokes. After surface plasma nitriding, the die completed 40 000 strokes with good surface. The die life is expected to exceed 200 000 strokes.展开更多
Microstructure and property of bearing steel with and without nitrogen addition were investigated by microstructural observation and hardness measurement after different heat treatment processing. Based on the microst...Microstructure and property of bearing steel with and without nitrogen addition were investigated by microstructural observation and hardness measurement after different heat treatment processing. Based on the microstructural observation of both 9Cr18 steel and X90N steel, it was found that nitrogen addition could effectively reduce the amount and size of coarse carbides and also refine the original austenite grain size. Due to addition of nitrogen, more austenite phase was found in X90N steel than in 9Cr18 steel. The retained austenite of X90N steel after quenching at 1050℃ could be reduced from about 60% to about 7 9% by cold treatment at -73℃ and subsequent tempering, and thus finally increased the hardness up to 60 HRC after low temperature tempering and to 63 HRC after high temperature tempering. Furthermore, both the wear and corrosion resistance of X90N steel were found much more superior than those of 9Cr18 steel, which was attributed to the addition of nitrogen. It was proposed at last that nitrogen alloying into the high chromium bearing steel was a promising way not only to refine the size of both carbides and austenite, but also to achieve high hardness, high wear property and improved corrosion resistance of the stainless bearing steel.展开更多
文摘The effects of rare earths(RE)-Mg-Ti compound modification on the structures and properties of high-carbon high speed steel(HSS) were researched.The impact toughness(α_k),the fracture toughness(K_(1c))and threshold of fatigue crack growth(ΔK_(th))are tested.The thermal fatigue test is done on a self-straining thermal fatigue tester,the wear test is done on a high temperature wear test machine.The results show that the matrix can be refined by the RE-Mg-Ti compound modification,the eutectic carbides are inclined to spheroidicize and are distributed evenly,the morphology and distribution of eutectic carbides are improved by appropriate RE-Mg-Ti complex modification.After RE-Mg-Ti compound modification,a little effects can be found on the strength,hardness and red hardness,but the fracture toughness(K_(1c)) and threshold of fatigue crack growth(△K_(th)) are improved in the meantime,the impact toughness (α_k) is increased by over one time,and the resistance to thermal fatigue and wear resistance at an elevated temperature are remarkably improved.
文摘A new hot-work die steel for hot stamping was developed, and used the die for mass production. The produced die showed good performance owing to its high heat conductivity and wear-resistant characteristics. Two different benchmarking hot-work die steels were investigated, and then compared in terms of their impact ductility, temper characteristics ,heat conductivity, and thermal stability. The result of the high-temperature friction wear test indicated that oxidative wear was the main mode in high temperature. On the basis of the comparison and test results, the alloying composition of the new hot-work die steel was especially designed. The new die steel showed good performance with good wear-resistant quality, as well as temper hardness and heat conductivity of HRC 50 and 34.3 W/（ m ~ K）, respectively. Furthermore, without surface plasma nitriding, the die made of the new steel had no obvious galling with 6 142 strokes. After surface plasma nitriding, the die completed 40 000 strokes with good surface. The die life is expected to exceed 200 000 strokes.
基金supported by National Natural Science Foundation of China (51371057)International Project Collaboration between CISRI (P.R.China) and COMTES FHT a.s (Czech Republic)
文摘Microstructure and property of bearing steel with and without nitrogen addition were investigated by microstructural observation and hardness measurement after different heat treatment processing. Based on the microstructural observation of both 9Cr18 steel and X90N steel, it was found that nitrogen addition could effectively reduce the amount and size of coarse carbides and also refine the original austenite grain size. Due to addition of nitrogen, more austenite phase was found in X90N steel than in 9Cr18 steel. The retained austenite of X90N steel after quenching at 1050℃ could be reduced from about 60% to about 7 9% by cold treatment at -73℃ and subsequent tempering, and thus finally increased the hardness up to 60 HRC after low temperature tempering and to 63 HRC after high temperature tempering. Furthermore, both the wear and corrosion resistance of X90N steel were found much more superior than those of 9Cr18 steel, which was attributed to the addition of nitrogen. It was proposed at last that nitrogen alloying into the high chromium bearing steel was a promising way not only to refine the size of both carbides and austenite, but also to achieve high hardness, high wear property and improved corrosion resistance of the stainless bearing steel.