YAG： Ce^3 ＋ phosphor particles were prepared using polyacrylamide gel method. The structure evolution of powders during annealing process was followed by X-ray diffraction determination. It is found that some interm...YAG： Ce^3 ＋ phosphor particles were prepared using polyacrylamide gel method. The structure evolution of powders during annealing process was followed by X-ray diffraction determination. It is found that some intermediate phases, including θ-Al2O3, YAM and YAP, are formed when calcining polyacrylamide gel, however, the pure YAG phase can be formed directly when calcining polyacrylamide gel with α-Al2O3 as seed crystal. These facts show that the existence of α- Al2O3 seed crystal can block the formation of θ-Al2O3, YAM and YAP, and accelerate its reaction with Y2O3 to form YAG phase directly at lower temperature. The emission peak of prepared YAG ： Ce^3 ＋ phosphor is wide with maximum at 550 nm and the exitation band has two peaks, the major one is around at 460 nm, which matches the blue emission of GaN LED and is suitable for the assemble of white LED. Some fluxes can enhance the photoluminescence intensity of phosphor particles, that can be attributed both to the improvement of crystallization processes of YAG and to the stabilization of trivalence cerium ion in YAG：Ce^3 ＋.展开更多
The crystallization behavior and kinetics of CaO-MgO-Al2O3 SiO2（CMAS） glass with the Fe2O3 content ranging from zero to 5%were investigated by differential scanning calorimetry（DSC）.The structure and phase analyse...The crystallization behavior and kinetics of CaO-MgO-Al2O3 SiO2（CMAS） glass with the Fe2O3 content ranging from zero to 5%were investigated by differential scanning calorimetry（DSC）.The structure and phase analyses were made by Fourier transform infrared spectroscopy（FT-IR） and X-ray diffraction（XRD）.The experiment results show that the endothermic peak temperature about 760℃ is associated with transition and the exothermic peak temperature about 1000℃ is associated with crystallization.The crystallization peak temperature decreases with increasing the Fe203 content.The crystallization mechanism is changed from two-dimensional crystallization to one-dimensional growth,and the intensity of diopside peaks becomes stronger gradually.There is a saltation for the crystallization temperature with the addition of 0.5%Fe2O3 due to the decomposition of Fe2O3.Si-O-Si,O-Si-O and T-O-T（T=Si,Fe,Al） linkages are observed in Fe2O3-CaO-MgO-Al2O3-SiO2 glass.展开更多
The capability of sol-gel and conventional precipitation techniques for the synthesis of nanocrystalline γ-alumina was investigated. These catalysts were used for vapor-phase dehydration of methanol to dimethyl ether...The capability of sol-gel and conventional precipitation techniques for the synthesis of nanocrystalline γ-alumina was investigated. These catalysts were used for vapor-phase dehydration of methanol to dimethyl ether in a fixed-bed reactor under the same operating conditions （T = 300 ？C, P = 1 bar, LHSV = 2.8, 11.7, 26.1 h？1） and characterized by means of N2 adsorption-desorption, NH3-TPD, XRD, TGA and SEM techniques. According to the experimental results, the catalysts prepared using sol-gel method in non-aqueous medium showed better performance compared with those prepared by other methods.展开更多
X-ray powder diffraction and Fourier transform infrared spectroscopy were applied for characterization of Li2O-Al2O3-SiO2 glass-ceramic powders doped with Eu2O3,Gd2O3 and Er2O3,respectively,in the conditions of differ...X-ray powder diffraction and Fourier transform infrared spectroscopy were applied for characterization of Li2O-Al2O3-SiO2 glass-ceramic powders doped with Eu2O3,Gd2O3 and Er2O3,respectively,in the conditions of different heat-treatment temperatures and with various amounts.The powders were derived from the polyacrylamide gel method.The results show that,the wet gels prepared by polyacrylamide perform a unique crystallization behavior in the process of drying,comparing with some customary preparation such as melt processing.The main crystal phase and crystallization sequence of Li2O-Al2O3-SiO2 micro-powders have no distinct with addition of Eu2O3,Gd2O3 or Er2O3,while the crystallization temperature of the β-spodumene decreased and the amount of the β-spodumene increased.展开更多
文摘YAG： Ce^3 ＋ phosphor particles were prepared using polyacrylamide gel method. The structure evolution of powders during annealing process was followed by X-ray diffraction determination. It is found that some intermediate phases, including θ-Al2O3, YAM and YAP, are formed when calcining polyacrylamide gel, however, the pure YAG phase can be formed directly when calcining polyacrylamide gel with α-Al2O3 as seed crystal. These facts show that the existence of α- Al2O3 seed crystal can block the formation of θ-Al2O3, YAM and YAP, and accelerate its reaction with Y2O3 to form YAG phase directly at lower temperature. The emission peak of prepared YAG ： Ce^3 ＋ phosphor is wide with maximum at 550 nm and the exitation band has two peaks, the major one is around at 460 nm, which matches the blue emission of GaN LED and is suitable for the assemble of white LED. Some fluxes can enhance the photoluminescence intensity of phosphor particles, that can be attributed both to the improvement of crystallization processes of YAG and to the stabilization of trivalence cerium ion in YAG：Ce^3 ＋.
基金Projects(51264023,51364020,U1202271)supported by the National Natural Science Foundation of ChinaProject(IRT1250)supported by the Program for Innovative Research Team in University of Ministry of Education of ChinaProject(2014HA003)supported by the Science and Technology Leading Talent of Yunnan Province,China
文摘The crystallization behavior and kinetics of CaO-MgO-Al2O3 SiO2（CMAS） glass with the Fe2O3 content ranging from zero to 5%were investigated by differential scanning calorimetry（DSC）.The structure and phase analyses were made by Fourier transform infrared spectroscopy（FT-IR） and X-ray diffraction（XRD）.The experiment results show that the endothermic peak temperature about 760℃ is associated with transition and the exothermic peak temperature about 1000℃ is associated with crystallization.The crystallization peak temperature decreases with increasing the Fe203 content.The crystallization mechanism is changed from two-dimensional crystallization to one-dimensional growth,and the intensity of diopside peaks becomes stronger gradually.There is a saltation for the crystallization temperature with the addition of 0.5%Fe2O3 due to the decomposition of Fe2O3.Si-O-Si,O-Si-O and T-O-T（T=Si,Fe,Al） linkages are observed in Fe2O3-CaO-MgO-Al2O3-SiO2 glass.
基金supported by Iranian Nanotechnology Initiative Council
文摘The capability of sol-gel and conventional precipitation techniques for the synthesis of nanocrystalline γ-alumina was investigated. These catalysts were used for vapor-phase dehydration of methanol to dimethyl ether in a fixed-bed reactor under the same operating conditions （T = 300 ？C, P = 1 bar, LHSV = 2.8, 11.7, 26.1 h？1） and characterized by means of N2 adsorption-desorption, NH3-TPD, XRD, TGA and SEM techniques. According to the experimental results, the catalysts prepared using sol-gel method in non-aqueous medium showed better performance compared with those prepared by other methods.
文摘X-ray powder diffraction and Fourier transform infrared spectroscopy were applied for characterization of Li2O-Al2O3-SiO2 glass-ceramic powders doped with Eu2O3,Gd2O3 and Er2O3,respectively,in the conditions of different heat-treatment temperatures and with various amounts.The powders were derived from the polyacrylamide gel method.The results show that,the wet gels prepared by polyacrylamide perform a unique crystallization behavior in the process of drying,comparing with some customary preparation such as melt processing.The main crystal phase and crystallization sequence of Li2O-Al2O3-SiO2 micro-powders have no distinct with addition of Eu2O3,Gd2O3 or Er2O3,while the crystallization temperature of the β-spodumene decreased and the amount of the β-spodumene increased.