To broaden the application of SiO_(2) sol-bonded castables,using micro-or nano-Al_(2)O_(3) powder and SiO_(2) gel powder as the main raw materials,the effects of CaO impurity on the formation of mullite by the reactio...To broaden the application of SiO_(2) sol-bonded castables,using micro-or nano-Al_(2)O_(3) powder and SiO_(2) gel powder as the main raw materials,the effects of CaO impurity on the formation of mullite by the reaction of Al_(2)O_(3) and SiO_(2) at different temperatures(1350,1400,1500,and 1600℃)in different atmospheres(oxidation atmosphere and reduction atmosphere)were studied.The results show that in the oxidizing atmosphere,the introduction of CaO can promote the formation of mullite.When the temperature increases from 1350℃to 1600℃,the amount of mullite formed gradually increases.In the reducing atmosphere,the introduction of CaO is not conducive to the formation of mullite,and the amount of mullite decreases with the increasing temperature.The smaller the particle size of Al_(2)O_(3),the more easily it reacts with SiO_(2) gel powder to form mullite.展开更多
A γ-TiAl alloy with nominal composition of Ti-47%Al（molar fraction） was directionally solidified in an alumina mould with an Y2O3 protective coating.The effects of processing parameters（melting temperature and int...A γ-TiAl alloy with nominal composition of Ti-47%Al（molar fraction） was directionally solidified in an alumina mould with an Y2O3 protective coating.The effects of processing parameters（melting temperature and interaction time） on the metal-coating interface,microstructure and chemical composition of the alloy were evaluated.The result shows that the Y2O3 protective coating exhibits an effective barrier capability to avoid direct contact between the mould base material and the TiAl melt,although the Y2O3 coating is found to suffer some erosion and be slightly dissolved by the molten TiAl due to the coating-metal interactions.The directionally solidified alloys were contaminated with Y and O,and Y2O3 inclusions were dispersed in the metal matrix.The reason for this metal contamination is the Y2O3 coating dissolution by the TiAl melt.One mode of the interaction between Y2O3 and the TiAl melt is dissolution of yttrium and atomic oxygen in the melt by reaction Y2O3（s）=2Y（in TiAl melt）＋3O（in TiAl melt）.Both the extent of alloy contamination and the volume fractions of Y2O3 inclusions depend on the melting temperature and the interaction time.展开更多
基金This work was financially supported by National Natural Science Foundation of China(Nos.52172031 and 51872266).
文摘To broaden the application of SiO_(2) sol-bonded castables,using micro-or nano-Al_(2)O_(3) powder and SiO_(2) gel powder as the main raw materials,the effects of CaO impurity on the formation of mullite by the reaction of Al_(2)O_(3) and SiO_(2) at different temperatures(1350,1400,1500,and 1600℃)in different atmospheres(oxidation atmosphere and reduction atmosphere)were studied.The results show that in the oxidizing atmosphere,the introduction of CaO can promote the formation of mullite.When the temperature increases from 1350℃to 1600℃,the amount of mullite formed gradually increases.In the reducing atmosphere,the introduction of CaO is not conducive to the formation of mullite,and the amount of mullite decreases with the increasing temperature.The smaller the particle size of Al_(2)O_(3),the more easily it reacts with SiO_(2) gel powder to form mullite.
文摘A γ-TiAl alloy with nominal composition of Ti-47%Al（molar fraction） was directionally solidified in an alumina mould with an Y2O3 protective coating.The effects of processing parameters（melting temperature and interaction time） on the metal-coating interface,microstructure and chemical composition of the alloy were evaluated.The result shows that the Y2O3 protective coating exhibits an effective barrier capability to avoid direct contact between the mould base material and the TiAl melt,although the Y2O3 coating is found to suffer some erosion and be slightly dissolved by the molten TiAl due to the coating-metal interactions.The directionally solidified alloys were contaminated with Y and O,and Y2O3 inclusions were dispersed in the metal matrix.The reason for this metal contamination is the Y2O3 coating dissolution by the TiAl melt.One mode of the interaction between Y2O3 and the TiAl melt is dissolution of yttrium and atomic oxygen in the melt by reaction Y2O3（s）=2Y（in TiAl melt）＋3O（in TiAl melt）.Both the extent of alloy contamination and the volume fractions of Y2O3 inclusions depend on the melting temperature and the interaction time.