A recycled aggregate(RA)was prepared by crushing and sieving demolished discarded concrete pavements and was subsequently tested and analyzed to determine its various physical properties.On this basis,pervious concre...A recycled aggregate(RA)was prepared by crushing and sieving demolished discarded concrete pavements and was subsequently tested and analyzed to determine its various physical properties.On this basis,pervious concrete(PC)mix proportions were designed.Coarse RA particles with sizes of 5–10 and 10–20 mm were selected.Concrete specimens were prepared with a water–cement ratio of 0.3,an aggregate–cement ratio of 4.5,the substitute rates of RA with 0,25%,50%,75%and a single-/double-gap-graded RA mix(mass ratio of particles with sizes of 5–10 mm to particles with sizes of 10–20 mm:1:1,1:2,2:1,2:3 and 3:2).Various properties of the RA-containing PC(RPC)were determined by analyzing the compressive strength,splitting tensile strength,effective porosity,permeation coefficient and impact and abrasion resistance of the specimens.The results showed the following:The density of the RPC decreased with an increasing RA replacement ratio.The density of the RPC prepared with a double-gapgraded RA mix was lower than that prepared with a single-gap-graded RA(particle size:10–20 mm)mix.The permeation coefficient of the RPC increased with increasing porosity.The splitting tensile strength of the RPC was positively correlated with its compressive strength.The compressive strength of the RPC decreased with increasing porosity.The regression analysis showed that the impact and abrasion resistance of the RPC increased with increasing compressive strength.In addition,all of the RPC specimens met the strength and permeation requirements.This study can provide theoretical support for the application of RPC.展开更多
In order to explore the relationship between the macroscopic properties and pore structure characteristics of baking-free slag-sludge bricks,the compressive strength and water absorption rate using aluminum industrial...In order to explore the relationship between the macroscopic properties and pore structure characteristics of baking-free slag-sludge bricks,the compressive strength and water absorption rate using aluminum industrial slag and sludge of different substitution rates were tested.Optical instruments and image analysis software were used to measure the parameters of the pore structure.Specifically,a fractal model was built based on the fractal theory,in which the fractal dimension was used as the characteristic index of the pore structure to analyze the correlation and interaction mechanism between the fractal dimension and the macroscopic mechanical properties.Based on this study,conclusions were drawn as follows:(1)The plane pore structure of baking-free bricks shows good fractal characteristics.With the increase of the aluminum industrial slag content,the fractal dimension becomes smaller and the pore structure develops well;with the increase of the sludge content,the fractal dimension becomes larger and the pore structure becomes worse;(2)As the fractal dimension of the plane pore structure increases,the compressive strength of baking-free bricks falls,and the porosity and water absorption rise;(3)The optimum content of baking-free slag-sludge bricks is aluminum industrial slag 30%and sludge 10%.After 7 days of curing,baking-free bricks boast higher performance,and fully meet the performance requirements of solid concrete bricks(MU40),which can reduce time costs,and enhance enterprise revenue.展开更多
基金This study was funded by the National key research and development program fund project(No.2018YFC0406803).
文摘A recycled aggregate(RA)was prepared by crushing and sieving demolished discarded concrete pavements and was subsequently tested and analyzed to determine its various physical properties.On this basis,pervious concrete(PC)mix proportions were designed.Coarse RA particles with sizes of 5–10 and 10–20 mm were selected.Concrete specimens were prepared with a water–cement ratio of 0.3,an aggregate–cement ratio of 4.5,the substitute rates of RA with 0,25%,50%,75%and a single-/double-gap-graded RA mix(mass ratio of particles with sizes of 5–10 mm to particles with sizes of 10–20 mm:1:1,1:2,2:1,2:3 and 3:2).Various properties of the RA-containing PC(RPC)were determined by analyzing the compressive strength,splitting tensile strength,effective porosity,permeation coefficient and impact and abrasion resistance of the specimens.The results showed the following:The density of the RPC decreased with an increasing RA replacement ratio.The density of the RPC prepared with a double-gapgraded RA mix was lower than that prepared with a single-gap-graded RA(particle size:10–20 mm)mix.The permeation coefficient of the RPC increased with increasing porosity.The splitting tensile strength of the RPC was positively correlated with its compressive strength.The compressive strength of the RPC decreased with increasing porosity.The regression analysis showed that the impact and abrasion resistance of the RPC increased with increasing compressive strength.In addition,all of the RPC specimens met the strength and permeation requirements.This study can provide theoretical support for the application of RPC.
基金Science and Technology Project of Henan Water Resources Department support program.No.GG202040Fund of Innovative Education Program for Graduate Students at North China University of Water Resources and Electric Power,China.No.YK2020-04.
文摘In order to explore the relationship between the macroscopic properties and pore structure characteristics of baking-free slag-sludge bricks,the compressive strength and water absorption rate using aluminum industrial slag and sludge of different substitution rates were tested.Optical instruments and image analysis software were used to measure the parameters of the pore structure.Specifically,a fractal model was built based on the fractal theory,in which the fractal dimension was used as the characteristic index of the pore structure to analyze the correlation and interaction mechanism between the fractal dimension and the macroscopic mechanical properties.Based on this study,conclusions were drawn as follows:(1)The plane pore structure of baking-free bricks shows good fractal characteristics.With the increase of the aluminum industrial slag content,the fractal dimension becomes smaller and the pore structure develops well;with the increase of the sludge content,the fractal dimension becomes larger and the pore structure becomes worse;(2)As the fractal dimension of the plane pore structure increases,the compressive strength of baking-free bricks falls,and the porosity and water absorption rise;(3)The optimum content of baking-free slag-sludge bricks is aluminum industrial slag 30%and sludge 10%.After 7 days of curing,baking-free bricks boast higher performance,and fully meet the performance requirements of solid concrete bricks(MU40),which can reduce time costs,and enhance enterprise revenue.