Mn-based intermetallic compounds have attracted much attention due to their fascinating structural and physical properties,especially their interesting hard magnetic properties.In this paper,we have summarized the mag...Mn-based intermetallic compounds have attracted much attention due to their fascinating structural and physical properties,especially their interesting hard magnetic properties.In this paper,we have summarized the magnetic and structural properties of Mn-based intermetallic compounds(Mn X,where X=Al,Bi,and Ga).Various methods for synthesizing single phases of MnAl,MnBi,and Mnx Ga were developed in our lab.A very high saturation magnetization of 125 emu/g,coercivity of 5 kOe,and maximum energy product(BH)_(max)of 3.1 MG·Oe were achieved at room temperature for the pureτ-Mn–Al magnetic phase without carbon doping and the extrusion process.Low temperature phase(LTP)MnBi with a purity above 95 wt.%can be synthesized.An abnormal temperature coefficient of the coercivity was observed for the LTP MnBi magnet.Its coercivity increased with temperature from 100 K to 540 K,reached a maximum of 2.5 T at about540 K,and then decreased slowly to 1.8 T at 610 K.The positive temperature coefficient of the coercivity is related to the evolution of the structure and magnetocrystalline anisotropy field of the LTP MnBi phase with temperature.The LTP MnBi bonded magnets show maximum energy products(BH)_(max)of 8.9 MG·Oe(70 kJ/m^(3))and 5.0 MG·Oe(40 k J/m^(3))at room temperature and 400 K,respectively.Ferrimagnetic Mn_(x)Ga phases with L10 structures(x〈2.0)and D0_(22)structures(x〉2.0)were obtained.All of the above structures can be described by a D0_(22)supercell model in which 2 a-Ga and 2 b-Mn are simultaneously substituted.The tetragonal D0_(22)phases of the Mn_(x)Ga show high coercivities ranging from 7.2 kOe for low Mn content x=1.8 to 18.2 kOe for high Mn content x=3 at room temperature.The Mn_(1.2)Ga sample exhibits a room temperature magnetization value of 80 emu/g.The hard magnetic properties of coercivityiH_(c)=3.5 kOe,remanence M_(r)=43.6 emu/g,and(BH)_(max)=2.5 MG·Oe were obtained at room temperature.Based on the above studies,we believe that Mn-based magnetic materials could be promising candidates for rare earth free permanent magnets exhibiting a high Curie temperature,high magnetocrystalline anisotropy,and very high coercivity.展开更多
基金Project supported by the National Natural Science Foundation of China(Grant Nos.51731001,11805006,51371009,11504348,and 11675006)National Key Research and Development Program of China(Grant Nos.2016YFB0700901,2017YFA0401502,and 2017YFA0206303)
文摘Mn-based intermetallic compounds have attracted much attention due to their fascinating structural and physical properties,especially their interesting hard magnetic properties.In this paper,we have summarized the magnetic and structural properties of Mn-based intermetallic compounds(Mn X,where X=Al,Bi,and Ga).Various methods for synthesizing single phases of MnAl,MnBi,and Mnx Ga were developed in our lab.A very high saturation magnetization of 125 emu/g,coercivity of 5 kOe,and maximum energy product(BH)_(max)of 3.1 MG·Oe were achieved at room temperature for the pureτ-Mn–Al magnetic phase without carbon doping and the extrusion process.Low temperature phase(LTP)MnBi with a purity above 95 wt.%can be synthesized.An abnormal temperature coefficient of the coercivity was observed for the LTP MnBi magnet.Its coercivity increased with temperature from 100 K to 540 K,reached a maximum of 2.5 T at about540 K,and then decreased slowly to 1.8 T at 610 K.The positive temperature coefficient of the coercivity is related to the evolution of the structure and magnetocrystalline anisotropy field of the LTP MnBi phase with temperature.The LTP MnBi bonded magnets show maximum energy products(BH)_(max)of 8.9 MG·Oe(70 kJ/m^(3))and 5.0 MG·Oe(40 k J/m^(3))at room temperature and 400 K,respectively.Ferrimagnetic Mn_(x)Ga phases with L10 structures(x〈2.0)and D0_(22)structures(x〉2.0)were obtained.All of the above structures can be described by a D0_(22)supercell model in which 2 a-Ga and 2 b-Mn are simultaneously substituted.The tetragonal D0_(22)phases of the Mn_(x)Ga show high coercivities ranging from 7.2 kOe for low Mn content x=1.8 to 18.2 kOe for high Mn content x=3 at room temperature.The Mn_(1.2)Ga sample exhibits a room temperature magnetization value of 80 emu/g.The hard magnetic properties of coercivityiH_(c)=3.5 kOe,remanence M_(r)=43.6 emu/g,and(BH)_(max)=2.5 MG·Oe were obtained at room temperature.Based on the above studies,we believe that Mn-based magnetic materials could be promising candidates for rare earth free permanent magnets exhibiting a high Curie temperature,high magnetocrystalline anisotropy,and very high coercivity.
