Ionic liquid(IL),1-butyl-3-methylimidazolium hexafluorophosphate([BMIM]PF6)as a new and environmentally friendly diluent was introduced to prepare poly(vinylidene fluoride)(PVDF)membranes via thermally induced phase s...Ionic liquid(IL),1-butyl-3-methylimidazolium hexafluorophosphate([BMIM]PF6)as a new and environmentally friendly diluent was introduced to prepare poly(vinylidene fluoride)(PVDF)membranes via thermally induced phase separation(TIPS).Phase diagram of PVDF/[BMIM]PF6 was measured.The effects of polymer concentration and quenching temperature on the morphologies,properties,and performances of the PVDF membranes were investigated.When the polymer concentration was 15 wt%,the pure water flux of the fabricated membrane was up to nearly 2000 L·m-2·h-1,along with adequate mechanical strength.With the increasing of PVDF concentration and quenching temperature,mean pore size and water permeability of the membrane decreased.SEM results showed that PVDF membranes manufactured by ionic liquid(BMIm PF6)presented spherulite structure.And the PVDF membranes were represented asβphase by XRD and FTIR characterization.It provides a new way to prepare PVDF membranes with piezoelectric properties.展开更多
Membrane fouling is the key problem that occurs in membrane process for water treatment. However, how membrane microstructure influences the fouling behavior is still not clear. In this study, fouling behavior caused ...Membrane fouling is the key problem that occurs in membrane process for water treatment. However, how membrane microstructure influences the fouling behavior is still not clear. In this study, fouling behavior caused by dextran was deeply and systematically investigated by employing four poly（vinylidene fluoride） （PVDF） membranes with different pore sizes, ranging from 24 to 94 nm. The extent of fouling by dextran was accurately characterized by pore reduction, flux decline, and the change of critical flux. The result shows that membrane with the smallest pore size of 24 nm experienced the smallest fouling rate and the lowest fouling extent. As the membrane pore size increased, the critical flux ranges were 105-114, 63-73, 38-44 and 34- 43 L. m 2. h t, respectively. The critical flux and fouling resistances indicated that the fouling propensity in- creases with the increase of membrane pore size. Two pilot membrane modules with mean pore size of 25 nm and 60 nm were applied in membrane filtration of surface water treatment. The results showed that serious ir- reversible membrane fouling occurred on the membrane with pore size of 60 nm at the permeate flux of 40.5 L.m 2.h 1. On the other hand, membrane with pore size of 25 nm exhibited much better anti-fouling per- formance when permeate flux was set to 40.5, 48 and 60 L-m 2-h- 1.展开更多
In the crystal engineering area,it is important to clearly demonstrating the relationship of structure and certain functionality.Herein,we present the study of the relationship of structure with phosphorescent nature ...In the crystal engineering area,it is important to clearly demonstrating the relationship of structure and certain functionality.Herein,we present the study of the relationship of structure with phosphorescent nature for two new room temperature phosphorescence(RTP) coordination polymers(CPs).[Pb(FDA)(H_(2)O)](1) and [NH_(3)(CH_(3))NH_(2)(CH_(3))_(2)][Pb_(4)(FDA)_(5)](2),where H_(2) FDA is 2,5-furandicarboxylic acid,have been synthesized by solvothermal method using different solvents and Pb^(2+) sources and characterized by microanalysis,powderX-ray diffraction(PXRD),thermogravimetric(TG),IR and UV-vis spectra.The Pb^(2+)ions adopt bicapped triangle prism coordination sphere in 1 and 2,which are connected together via FDA^(2-) ligands into bilayer structure in 1 while pillared-layer framework in 2.The FDA^(2-) ligands show different bridging modes in 1 and 2,leading to distinct coordination interactions between Pb^(2+) ion and FDA^(2-) ligand in both CPs.Both 1 and 2 emit ligand-centered RTP due to the heavy atom of Pb^(2+) ion,with a lifetime and quantum yield of 0.62 ms and 14.9% in 1 versus 1.69 ms and 15.7% in 2.The emission peak shows significant redshift(79 nm) in 2 regarding 1,which arises from their distinction of coordination interactions between Pb^(2+) ion and FDA^(2-) ligand in both CPs.展开更多
基金the financial support of the National Natural Science Foundation of China(Grant No.21606125)the Natural Science Foundation of Jiangsu Province(Grant No.BK20160984)+3 种基金the National Key R&D Program of China(Grant No.2017YFC0403702)the Materials-Oriented Chemical Engineering State Key Laboratory Program(KL16-09)the open project program of Jiangsu Key Lab for Chemistry of Low-Dimensional Materials(JSKC17005)the Priority Academic Program Development of Jiangsu Higher Education Institution(PAPD)。
文摘Ionic liquid(IL),1-butyl-3-methylimidazolium hexafluorophosphate([BMIM]PF6)as a new and environmentally friendly diluent was introduced to prepare poly(vinylidene fluoride)(PVDF)membranes via thermally induced phase separation(TIPS).Phase diagram of PVDF/[BMIM]PF6 was measured.The effects of polymer concentration and quenching temperature on the morphologies,properties,and performances of the PVDF membranes were investigated.When the polymer concentration was 15 wt%,the pure water flux of the fabricated membrane was up to nearly 2000 L·m-2·h-1,along with adequate mechanical strength.With the increasing of PVDF concentration and quenching temperature,mean pore size and water permeability of the membrane decreased.SEM results showed that PVDF membranes manufactured by ionic liquid(BMIm PF6)presented spherulite structure.And the PVDF membranes were represented asβphase by XRD and FTIR characterization.It provides a new way to prepare PVDF membranes with piezoelectric properties.
基金Supported by the National Natural Science Foundation of China(2160060639)the Natural Science Foundation of Jiangsu Province(BK20160984)the Scientific Research Foundation for Returned Overseas Chinese Scholars,State Education Ministry(ZX15511310002)
文摘Membrane fouling is the key problem that occurs in membrane process for water treatment. However, how membrane microstructure influences the fouling behavior is still not clear. In this study, fouling behavior caused by dextran was deeply and systematically investigated by employing four poly（vinylidene fluoride） （PVDF） membranes with different pore sizes, ranging from 24 to 94 nm. The extent of fouling by dextran was accurately characterized by pore reduction, flux decline, and the change of critical flux. The result shows that membrane with the smallest pore size of 24 nm experienced the smallest fouling rate and the lowest fouling extent. As the membrane pore size increased, the critical flux ranges were 105-114, 63-73, 38-44 and 34- 43 L. m 2. h t, respectively. The critical flux and fouling resistances indicated that the fouling propensity in- creases with the increase of membrane pore size. Two pilot membrane modules with mean pore size of 25 nm and 60 nm were applied in membrane filtration of surface water treatment. The results showed that serious ir- reversible membrane fouling occurred on the membrane with pore size of 60 nm at the permeate flux of 40.5 L.m 2.h 1. On the other hand, membrane with pore size of 25 nm exhibited much better anti-fouling per- formance when permeate flux was set to 40.5, 48 and 60 L-m 2-h- 1.
基金the National Natural Science Foundation of China (No.21901116)。
文摘In the crystal engineering area,it is important to clearly demonstrating the relationship of structure and certain functionality.Herein,we present the study of the relationship of structure with phosphorescent nature for two new room temperature phosphorescence(RTP) coordination polymers(CPs).[Pb(FDA)(H_(2)O)](1) and [NH_(3)(CH_(3))NH_(2)(CH_(3))_(2)][Pb_(4)(FDA)_(5)](2),where H_(2) FDA is 2,5-furandicarboxylic acid,have been synthesized by solvothermal method using different solvents and Pb^(2+) sources and characterized by microanalysis,powderX-ray diffraction(PXRD),thermogravimetric(TG),IR and UV-vis spectra.The Pb^(2+)ions adopt bicapped triangle prism coordination sphere in 1 and 2,which are connected together via FDA^(2-) ligands into bilayer structure in 1 while pillared-layer framework in 2.The FDA^(2-) ligands show different bridging modes in 1 and 2,leading to distinct coordination interactions between Pb^(2+) ion and FDA^(2-) ligand in both CPs.Both 1 and 2 emit ligand-centered RTP due to the heavy atom of Pb^(2+) ion,with a lifetime and quantum yield of 0.62 ms and 14.9% in 1 versus 1.69 ms and 15.7% in 2.The emission peak shows significant redshift(79 nm) in 2 regarding 1,which arises from their distinction of coordination interactions between Pb^(2+) ion and FDA^(2-) ligand in both CPs.