The giant magnetoimpedance effect of the nanocrystalline ribbonFe_(84)Zr_(2.08)Nb_(1.92)Cu_1B_(11) (atom fraction in %) was investigated. There is an optimumannealing temperature (T_A≈ 998 K) for obtaining the larges...The giant magnetoimpedance effect of the nanocrystalline ribbonFe_(84)Zr_(2.08)Nb_(1.92)Cu_1B_(11) (atom fraction in %) was investigated. There is an optimumannealing temperature (T_A≈ 998 K) for obtaining the largest GMI (giant magneto-impedance) effectin the ribbon Fe_(84)Zr_(2.08)Nb_(1.92)Cu_1B_(11). The ribbon with longer ribbon length has strongerGMI effect, which may be connected with the demagnetization effect of samples. The frequencyf_(max), where the maximum magnetoimpedance GMI(Z)_(max) = [(Z(H) - Z(0))/Z(0)]_(max) occurs, isnear the intersecting frequency f_i of the curves of GMI(R), GMI(X), and GMI(Z) versus frequency.The magnetoreactance GMI(X) decreases monotonically with increasing frequency, which may be due tothe decrease of permeability. In contrast, with the AC (alternating current) frequency increasing,the inagnetore-sistance GMI(R) increases at first, undergoes a peak, and under then drops. Theincrease of the magnetoresistance may result from the enhancement of the skin effect with frequency.The maximum magnetoimpedance value GMI(Z)_(max) under H = 7.2 kA/m is about -56.18% at f= 0.3 MHzfor the nanocrystalline ribbon Fe_(84)Zr_(2.08)Nb_(1.92)Cu_1B_(11) with the annealing temperatureT_A= 998 K and the ribbon length L = 6 cm.展开更多
基金This work was financially supported by the National Natural Science Foundation of China (No. 50271036)
文摘The giant magnetoimpedance effect of the nanocrystalline ribbonFe_(84)Zr_(2.08)Nb_(1.92)Cu_1B_(11) (atom fraction in %) was investigated. There is an optimumannealing temperature (T_A≈ 998 K) for obtaining the largest GMI (giant magneto-impedance) effectin the ribbon Fe_(84)Zr_(2.08)Nb_(1.92)Cu_1B_(11). The ribbon with longer ribbon length has strongerGMI effect, which may be connected with the demagnetization effect of samples. The frequencyf_(max), where the maximum magnetoimpedance GMI(Z)_(max) = [(Z(H) - Z(0))/Z(0)]_(max) occurs, isnear the intersecting frequency f_i of the curves of GMI(R), GMI(X), and GMI(Z) versus frequency.The magnetoreactance GMI(X) decreases monotonically with increasing frequency, which may be due tothe decrease of permeability. In contrast, with the AC (alternating current) frequency increasing,the inagnetore-sistance GMI(R) increases at first, undergoes a peak, and under then drops. Theincrease of the magnetoresistance may result from the enhancement of the skin effect with frequency.The maximum magnetoimpedance value GMI(Z)_(max) under H = 7.2 kA/m is about -56.18% at f= 0.3 MHzfor the nanocrystalline ribbon Fe_(84)Zr_(2.08)Nb_(1.92)Cu_1B_(11) with the annealing temperatureT_A= 998 K and the ribbon length L = 6 cm.