Monodisperse SiO_(2) microspheres have found applications in catalysis,drug delivery,coatings,cosmetics,optical sensing and plastics.The particle size of monodisperse SiO_(2) microspheres is closely related to its app...Monodisperse SiO_(2) microspheres have found applications in catalysis,drug delivery,coatings,cosmetics,optical sensing and plastics.The particle size of monodisperse SiO_(2) microspheres is closely related to its application.In this paper,monodisperse SiO_(2) microspheres with tunable diameter were successfully synthesized using cetyltrimethylammonium bromide(CTAB)as template.The monodisperse SiO_(2) microspheres with diameters ranging from 200 nm to 3μm were obtained by controlling the concentration of CTAB,tetraethyl orthosilicate(TEOS),diethanolamine(DEA)and reaction temperature.The BET surface area could reach 835 m^(2)·g^(-1) and mean pore diameter was 2.3 nm.The formation mechanism of monodisperse SiO_(2) microspheres was investigated.展开更多
基金supported by Jiangxi Provincial Department of Science and Technology(Nos.20192BBEL50017 and 20202ACBL203002)the National Natural Science Foundation of China(No.91622105).
文摘Monodisperse SiO_(2) microspheres have found applications in catalysis,drug delivery,coatings,cosmetics,optical sensing and plastics.The particle size of monodisperse SiO_(2) microspheres is closely related to its application.In this paper,monodisperse SiO_(2) microspheres with tunable diameter were successfully synthesized using cetyltrimethylammonium bromide(CTAB)as template.The monodisperse SiO_(2) microspheres with diameters ranging from 200 nm to 3μm were obtained by controlling the concentration of CTAB,tetraethyl orthosilicate(TEOS),diethanolamine(DEA)and reaction temperature.The BET surface area could reach 835 m^(2)·g^(-1) and mean pore diameter was 2.3 nm.The formation mechanism of monodisperse SiO_(2) microspheres was investigated.
基金National Natural Science Foundation of China (Grant Nos.21641008and 91622105) Jiangxi Provincial Department of Science and Technology (Grant Nos. 20161BAB203083 and 20172BCB22008).