Pure cobalt(Co)thin films were fabricated by direct current magnetron sputtering,and the effects of sputtering power and pres-sure on the microstructure and electromagnetic properties of the films were investigated.As...Pure cobalt(Co)thin films were fabricated by direct current magnetron sputtering,and the effects of sputtering power and pres-sure on the microstructure and electromagnetic properties of the films were investigated.As the sputtering power increases from 15 to 60 W,the Co thin films transition from an amorphous to a polycrystalline state,accompanied by an increase in the intercrystal pore width.Simultaneously,the resistivity decreases from 276 to 99μΩ·cm,coercivity increases from 162 to 293 Oe,and in-plane magnetic aniso-tropy disappears.As the sputtering pressure decreases from 1.6 to 0.2 Pa,grain size significantly increases,resistivity significantly de-creases,and the coercivity significantly increases(from 67 to 280 Oe),which can be attributed to the increase in defect width.Corres-pondingly,a quantitative model for the coercivity of Co thin films was formulated.The polycrystalline films sputtered under pressures of 0.2 and 0.4 Pa exhibit significant in-plane magnetic anisotropy,which is primarily attributable to increased microstress.展开更多
The service life and properties of Carbon fiber reinforced polycarbonate (CF/PC) composites are seriously affected by ultraviolet radiation from outdoor exposure during aging. In this work, the changes of structure an...The service life and properties of Carbon fiber reinforced polycarbonate (CF/PC) composites are seriously affected by ultraviolet radiation from outdoor exposure during aging. In this work, the changes of structure and solid particle erosion resistance for CF/PC composites after ultraviolet irradiation were studied. It was shown that ultraviolet irradiation causes photo-oxygen aging and photo-fries re-arrangement of the composite, and the result was confirmed by FTIR. We correlated the solid particle erosion resistance with aging time, and found that the solid particle erosion resistance of CF/PC composites greatly decreased by UVB irradiation during 15 hours. Furthermore, the eroded material surface was analyzed using scanning electron microscope (SEM). It suggests that ultraviolet aging leads to plasticization and degradation, resulting in reduction of erosion resistance of the composite.展开更多
基金the financial support from the National Key Research and Development Program of China(No.2017YFB0305500)the State Key Laboratory of Powder Metallurgy,Central South University,Changsha,China.
文摘Pure cobalt(Co)thin films were fabricated by direct current magnetron sputtering,and the effects of sputtering power and pres-sure on the microstructure and electromagnetic properties of the films were investigated.As the sputtering power increases from 15 to 60 W,the Co thin films transition from an amorphous to a polycrystalline state,accompanied by an increase in the intercrystal pore width.Simultaneously,the resistivity decreases from 276 to 99μΩ·cm,coercivity increases from 162 to 293 Oe,and in-plane magnetic aniso-tropy disappears.As the sputtering pressure decreases from 1.6 to 0.2 Pa,grain size significantly increases,resistivity significantly de-creases,and the coercivity significantly increases(from 67 to 280 Oe),which can be attributed to the increase in defect width.Corres-pondingly,a quantitative model for the coercivity of Co thin films was formulated.The polycrystalline films sputtered under pressures of 0.2 and 0.4 Pa exhibit significant in-plane magnetic anisotropy,which is primarily attributable to increased microstress.
文摘The service life and properties of Carbon fiber reinforced polycarbonate (CF/PC) composites are seriously affected by ultraviolet radiation from outdoor exposure during aging. In this work, the changes of structure and solid particle erosion resistance for CF/PC composites after ultraviolet irradiation were studied. It was shown that ultraviolet irradiation causes photo-oxygen aging and photo-fries re-arrangement of the composite, and the result was confirmed by FTIR. We correlated the solid particle erosion resistance with aging time, and found that the solid particle erosion resistance of CF/PC composites greatly decreased by UVB irradiation during 15 hours. Furthermore, the eroded material surface was analyzed using scanning electron microscope (SEM). It suggests that ultraviolet aging leads to plasticization and degradation, resulting in reduction of erosion resistance of the composite.