Sol-gel coatings containing various amounts of hydroxylated nanodiamond(HND)particles were applied on the magnesium alloy for corrosion protection.The micrometric defects in the sol-gel coating completely disappeared ...Sol-gel coatings containing various amounts of hydroxylated nanodiamond(HND)particles were applied on the magnesium alloy for corrosion protection.The micrometric defects in the sol-gel coating completely disappeared after adding 0.01,0.02 and 0.05 wt.%of the HND nanoparticles.The AFM analyses showed that average roughness of the sol-gel film is about 6.7 nm which increases to 16.1 and 20.2 nm after incorporating 0.005 and 0.02 wt.%of the HNDs,respectively.The corrosion resistance of the coatings was tested in Harrison’s solution by means of EIS technique after 15,30,60 and 120 min immersion.The corrosion resistance of the sol-gel coating was remarkably enhanced by incorporating different contents of the HNDs and the best result was obtained for 0.01 wt.%.The results of the EIS experiments were confirmed by the potentiodynamic polarization tests.The corrosion resistance enhancement was attributed to the film compactness(due to the chemical interaction with the HNDs),formation of tortuous pathways for diffusion of the corrosive solution,and filling of the defects by the nanoparticles.However,the beneficial effect of the HNDs on the corrosion resistance gradually diminished as the content of nanoparticle was increased.Finally,the micromorphology of the sol-gel nanocomposites was studied after the corrosion tests.展开更多
A microwave-assisted (4-6 min) method was used for the preparation of CdS nanoparticles in 1-ethyl-3-methylimidazolium ethyl sulfate,a halide-free room-temperature ionic liquid (RTIL).The samples were characterized by...A microwave-assisted (4-6 min) method was used for the preparation of CdS nanoparticles in 1-ethyl-3-methylimidazolium ethyl sulfate,a halide-free room-temperature ionic liquid (RTIL).The samples were characterized by powder X-ray diffraction,energy dispersive X-ray spectroscopy,and scanning electron microscopy.Diffuse reflectance spectra showed a 1.33 eV blue shift relative to bulk CdS.The photocatalytic activities of the nanoparticles for photodegradation of methylene blue (MB) using UV and visible light were measured.The photodegradation of MB decreased with calcination temperature.First order rate constants for the reaction under visible and UV irradiations over the nanoparticles prepared in the RTIL rich media were 5.4 and 2.5 higher,respectively,than the sample prepared in water.展开更多
Electrochemically promoted electroless plating(EPEP)was used for the application of pretreatment-free Ni-P coating on AM60B magnesium alloy at low temperatures and the obtained coating was characterized by SEM,AFM,EDS...Electrochemically promoted electroless plating(EPEP)was used for the application of pretreatment-free Ni-P coating on AM60B magnesium alloy at low temperatures and the obtained coating was characterized by SEM,AFM,EDS and XRD techniques.Compact,uniform,and medium-phosphorus Ni-P coating with mixed crystalline-amorphous microstructure was obtained by applying a cathodic current density of4mA/cm^2at50℃.Also,island-like nickel clusters were deposited on the alloy surface under the same plating condition but without applying the cathodic current.In addition,the durability of the magnesium alloy against corrosion was strongly improved after plating via EPEP technique which was revealed by electrochemical examinations in3.5%NaCl(mass fraction)corrosive electrolyte.The results of the electrochemical examinations were confirmed by microscopic observations.Thickness,microhardness,porosity and adhesive strength of the deposits were also qualified.展开更多
Continuous noise resistance calculation(CNRC)technique was used for online determination of the electroless nickel deposition rate on zirconium pretreated magnesium alloy.For this purpose,the noise resistance(R_n) var...Continuous noise resistance calculation(CNRC)technique was used for online determination of the electroless nickel deposition rate on zirconium pretreated magnesium alloy.For this purpose,the noise resistance(R_n) variation with time was calculated for the pretreated alloy surface in the electroless plating solution.The CNRC results were described by energy dispersive X-ray spectroscopy(EDS)and scanning electron microscopy(SEM)techniques.Also,potentiodynamic polarization and gravimetric measurements were used for determination of the electroless deposition rate at the same time period and the results were compared with the CNRC results.The Rn variation with plating time shows that the electroless plating consists of different stages with various deposition rates.The results of the CNRC and polarization methods were not in acceptable agreement due to the limitations of the polarization method for online monitoring of the deposition rate.However,the results of the gravimetric measurements were in complete agreement with the CNRC technique and so,the CNRC can be considered as suitable tool for online evaluation of the electroless deposition rate.展开更多
文摘Sol-gel coatings containing various amounts of hydroxylated nanodiamond(HND)particles were applied on the magnesium alloy for corrosion protection.The micrometric defects in the sol-gel coating completely disappeared after adding 0.01,0.02 and 0.05 wt.%of the HND nanoparticles.The AFM analyses showed that average roughness of the sol-gel film is about 6.7 nm which increases to 16.1 and 20.2 nm after incorporating 0.005 and 0.02 wt.%of the HNDs,respectively.The corrosion resistance of the coatings was tested in Harrison’s solution by means of EIS technique after 15,30,60 and 120 min immersion.The corrosion resistance of the sol-gel coating was remarkably enhanced by incorporating different contents of the HNDs and the best result was obtained for 0.01 wt.%.The results of the EIS experiments were confirmed by the potentiodynamic polarization tests.The corrosion resistance enhancement was attributed to the film compactness(due to the chemical interaction with the HNDs),formation of tortuous pathways for diffusion of the corrosive solution,and filling of the defects by the nanoparticles.However,the beneficial effect of the HNDs on the corrosion resistance gradually diminished as the content of nanoparticle was increased.Finally,the micromorphology of the sol-gel nanocomposites was studied after the corrosion tests.
文摘A microwave-assisted (4-6 min) method was used for the preparation of CdS nanoparticles in 1-ethyl-3-methylimidazolium ethyl sulfate,a halide-free room-temperature ionic liquid (RTIL).The samples were characterized by powder X-ray diffraction,energy dispersive X-ray spectroscopy,and scanning electron microscopy.Diffuse reflectance spectra showed a 1.33 eV blue shift relative to bulk CdS.The photocatalytic activities of the nanoparticles for photodegradation of methylene blue (MB) using UV and visible light were measured.The photodegradation of MB decreased with calcination temperature.First order rate constants for the reaction under visible and UV irradiations over the nanoparticles prepared in the RTIL rich media were 5.4 and 2.5 higher,respectively,than the sample prepared in water.
文摘Electrochemically promoted electroless plating(EPEP)was used for the application of pretreatment-free Ni-P coating on AM60B magnesium alloy at low temperatures and the obtained coating was characterized by SEM,AFM,EDS and XRD techniques.Compact,uniform,and medium-phosphorus Ni-P coating with mixed crystalline-amorphous microstructure was obtained by applying a cathodic current density of4mA/cm^2at50℃.Also,island-like nickel clusters were deposited on the alloy surface under the same plating condition but without applying the cathodic current.In addition,the durability of the magnesium alloy against corrosion was strongly improved after plating via EPEP technique which was revealed by electrochemical examinations in3.5%NaCl(mass fraction)corrosive electrolyte.The results of the electrochemical examinations were confirmed by microscopic observations.Thickness,microhardness,porosity and adhesive strength of the deposits were also qualified.
文摘Continuous noise resistance calculation(CNRC)technique was used for online determination of the electroless nickel deposition rate on zirconium pretreated magnesium alloy.For this purpose,the noise resistance(R_n) variation with time was calculated for the pretreated alloy surface in the electroless plating solution.The CNRC results were described by energy dispersive X-ray spectroscopy(EDS)and scanning electron microscopy(SEM)techniques.Also,potentiodynamic polarization and gravimetric measurements were used for determination of the electroless deposition rate at the same time period and the results were compared with the CNRC results.The Rn variation with plating time shows that the electroless plating consists of different stages with various deposition rates.The results of the CNRC and polarization methods were not in acceptable agreement due to the limitations of the polarization method for online monitoring of the deposition rate.However,the results of the gravimetric measurements were in complete agreement with the CNRC technique and so,the CNRC can be considered as suitable tool for online evaluation of the electroless deposition rate.