The formation of nanoporous Pd was studied by electro-chemical dealloying a rapidly-quenched Al70Pd17Fe13 quasicrystal alloy in dilute NaCl aqueous solution,and the electro-catalytic activity of the nanoporous Pd towa...The formation of nanoporous Pd was studied by electro-chemical dealloying a rapidly-quenched Al70Pd17Fe13 quasicrystal alloy in dilute NaCl aqueous solution,and the electro-catalytic activity of the nanoporous Pd towards methanol electro-oxidation was evaluated by cyclic voltammetry in 1 mol/L KOH solution.XRD and TEM analyses revealed that nano-decomposition of quasicrystal grains occurred in the initial stage of dealloying,and the fully dealloyed sample was composed of FCC-Pd phase.Scanning electron microscopy observation indicated that a maze-like nanoporous pattern was formed in the dealloyed sample,consisting of percolated pores of 5.20 nm in diameter in a skeleton of randomly-orientated Pd nano-ligaments with a uniform thickness of^5 nm.A retention of^12 at.%Al in the Pd nano-ligments was determined by energy dispersive X-ray spectroscopy(EDS).The nanoporous Pd demonstrated obvious electro-catalytic activity towards methanol electro-oxidation in alkaline environment.展开更多
研究了Co含量对熔体快淬Fe_(55-x)Co_xPt_(15)B_(30)(x=0~45,原子分数,%)合金热处理前后的组织结构和磁性能的影响。结果表明,添加Co可提高Fe_(55-x)Co_xPt_(15)B_(30)合金的非晶形成能力,使x=15~45的快淬合金形成非晶态。经适当热处理...研究了Co含量对熔体快淬Fe_(55-x)Co_xPt_(15)B_(30)(x=0~45,原子分数,%)合金热处理前后的组织结构和磁性能的影响。结果表明,添加Co可提高Fe_(55-x)Co_xPt_(15)B_(30)合金的非晶形成能力,使x=15~45的快淬合金形成非晶态。经适当热处理后,合金中形成了由有序面心四方结构的永磁(Fe,Co)-Pt(L1_0)相和软磁(Fe,Co)2B相及(Fe,Co)B相组成的纳米复相组织,显示出永磁性;添加Co的合金组织得到明显细化,x=15~45合金平均晶粒尺寸均约为18 nm;其中x=15合金具有最佳的永磁性能,磁能积达到94.4 k J/m3。合金的矫顽力随Co含量的增加而增大,在x=30时达到最大值413.7 k A/m后,随Co含量的进一步增加而减小;这是由于不同Co含量使L1_0相的c/a值发生变化而导致其磁晶各向异性变化的结果。展开更多
文摘目的针对某车载油箱高周疲劳寿命难以预测问题,研究该设备在随机载荷环境下的疲劳寿命。方法首先通过模态试验得到油箱固有频率及振型,然后利用Solidworks建立该车载油箱的仿真模型,在ANSYS Workbench软件中进行模态分析、随机振动分析、谐响应分析。最后利用ANSYS Workbench软件中的nCode SN Vibration(DesignLife)模块,在随机振动疲劳寿命频域分析法基础上,通过nCode模块中的Narrowband法进行油箱在多个加速度功率谱密度下的疲劳寿命研究。结果该油箱在约束模态试验和仿真分析下所表现的动力学特性基本相同,油箱纵向为振动严酷方向。在已知加速度功率谱密度下,油箱疲劳寿命随低阶固有频率处功率谱密度幅值的增加而降低,但油箱薄弱部位始终保持不变。结论建立的仿真模型准确,可为油箱优化设计及后续油箱疲劳试验提供参考。
基金Foundation item:Project(51671045)supported by the National Natural Science Foundation of ChinaProject(DUT18GF112)supported by the Fundamental Research Funds for the Central Universities,ChinaProject(TZ2016004)supported by the Science Challenge Project,China
文摘The formation of nanoporous Pd was studied by electro-chemical dealloying a rapidly-quenched Al70Pd17Fe13 quasicrystal alloy in dilute NaCl aqueous solution,and the electro-catalytic activity of the nanoporous Pd towards methanol electro-oxidation was evaluated by cyclic voltammetry in 1 mol/L KOH solution.XRD and TEM analyses revealed that nano-decomposition of quasicrystal grains occurred in the initial stage of dealloying,and the fully dealloyed sample was composed of FCC-Pd phase.Scanning electron microscopy observation indicated that a maze-like nanoporous pattern was formed in the dealloyed sample,consisting of percolated pores of 5.20 nm in diameter in a skeleton of randomly-orientated Pd nano-ligaments with a uniform thickness of^5 nm.A retention of^12 at.%Al in the Pd nano-ligments was determined by energy dispersive X-ray spectroscopy(EDS).The nanoporous Pd demonstrated obvious electro-catalytic activity towards methanol electro-oxidation in alkaline environment.
文摘研究了Co含量对熔体快淬Fe_(55-x)Co_xPt_(15)B_(30)(x=0~45,原子分数,%)合金热处理前后的组织结构和磁性能的影响。结果表明,添加Co可提高Fe_(55-x)Co_xPt_(15)B_(30)合金的非晶形成能力,使x=15~45的快淬合金形成非晶态。经适当热处理后,合金中形成了由有序面心四方结构的永磁(Fe,Co)-Pt(L1_0)相和软磁(Fe,Co)2B相及(Fe,Co)B相组成的纳米复相组织,显示出永磁性;添加Co的合金组织得到明显细化,x=15~45合金平均晶粒尺寸均约为18 nm;其中x=15合金具有最佳的永磁性能,磁能积达到94.4 k J/m3。合金的矫顽力随Co含量的增加而增大,在x=30时达到最大值413.7 k A/m后,随Co含量的进一步增加而减小;这是由于不同Co含量使L1_0相的c/a值发生变化而导致其磁晶各向异性变化的结果。