Lithium(Li)metal anodes have the potential to stimulate the development of secondary batteries due to their high theoretical specific capacities and low redox potentials among all possible solid secondary anode compou...Lithium(Li)metal anodes have the potential to stimulate the development of secondary batteries due to their high theoretical specific capacities and low redox potentials among all possible solid secondary anode compounds.However,the growth of Li dendrites during repeated Li stripping/plating processes leads to low coulombic efficiencies(CEs)and safety hazards,which significantly hinders their practical application.In this work,commercial Cu foil was modified in situ by Cu_(3)N nanowires(Cu_(3)N NWs/Cu)and used as the current collector for a Li anode.In addition to decreasing the true current density of the anode and alleviating the volume change during the cycles,Cu_(3)N reacted with Li during the initial cycle(3Li+Cu_(3)N→Li_(3)N+3Cu),which enabled the formation of a Li_(3)N-rich solid electrolyte interphase(SEI).This Li_(3)N-rich SEI with a high ionic conductivity not only boosted Li ion transport but also promoted the homogeneous deposition of Li via increased Li nucleation sites.The improvements in both mass transport and deposition dynamics restrained dendrite growth.As a result,the Cu_(3)N NWs/Cu anode had stable Li plating/stripping over 270 cycles with a high average CE of 98.6% at 1 mA cm^(-2),with Li capacities of 1 mA h cm^(-2).A long cycling lifespan of 430 cycles was achieved using a full cell with a high-load LiFePO_(4) cathode(mass loading:10 mg cm^(-2))and a Cu_(3)N NWs/Cu-Li anode(N/P=2.35),demonstrating the effectiveness and practicality of the Cu_(3)N NWs/Cu current collector in stabilizing the Li anode.展开更多
基金supported by the National Natural Science Foundation of China(22075091)the Natural Science Foundation of Hubei Province(2021CFA066)the“Fundamental Research Funds for the Central Universities”(2021yjsCXCY026)。
文摘Lithium(Li)metal anodes have the potential to stimulate the development of secondary batteries due to their high theoretical specific capacities and low redox potentials among all possible solid secondary anode compounds.However,the growth of Li dendrites during repeated Li stripping/plating processes leads to low coulombic efficiencies(CEs)and safety hazards,which significantly hinders their practical application.In this work,commercial Cu foil was modified in situ by Cu_(3)N nanowires(Cu_(3)N NWs/Cu)and used as the current collector for a Li anode.In addition to decreasing the true current density of the anode and alleviating the volume change during the cycles,Cu_(3)N reacted with Li during the initial cycle(3Li+Cu_(3)N→Li_(3)N+3Cu),which enabled the formation of a Li_(3)N-rich solid electrolyte interphase(SEI).This Li_(3)N-rich SEI with a high ionic conductivity not only boosted Li ion transport but also promoted the homogeneous deposition of Li via increased Li nucleation sites.The improvements in both mass transport and deposition dynamics restrained dendrite growth.As a result,the Cu_(3)N NWs/Cu anode had stable Li plating/stripping over 270 cycles with a high average CE of 98.6% at 1 mA cm^(-2),with Li capacities of 1 mA h cm^(-2).A long cycling lifespan of 430 cycles was achieved using a full cell with a high-load LiFePO_(4) cathode(mass loading:10 mg cm^(-2))and a Cu_(3)N NWs/Cu-Li anode(N/P=2.35),demonstrating the effectiveness and practicality of the Cu_(3)N NWs/Cu current collector in stabilizing the Li anode.
