A facile surface segregation method was utilized to fabricate poly（vinyl alcohol）-polyethersulfone （PVA-PES） composite membranes. PVA and PES were first dissolved in dimethyl sulfoxide （DMSO）, then casted on a g...A facile surface segregation method was utilized to fabricate poly（vinyl alcohol）-polyethersulfone （PVA-PES） composite membranes. PVA and PES were first dissolved in dimethyl sulfoxide （DMSO）, then casted on a glass plate and immersed in a coagulation bath. During the phase inversion process in coagulation bath, PVA spontaneously segregated to the polymer solution/coagulation bath interface. The enriched PVA on the surface was further crosslinked by glutaraldehyde. Scanning electron microscopy （SEM）, X-ray photoelectron spectroscopy （XPS） and energy dispersive spectrometer （EDS） confirmed the integral and asymmetric membrane structure with a dense PVA-enriched surface and a porous PES-enriched support, as well as the surface enrichment of PVA. The coverage fraction of the membrane surtace by PVA reacned up to 86.8% when me PVA content m me membrane recipe was 16.7% （by mass）. The water contact angle decreased with the increase of PVA content. The effect of coagulation bath type on membrane structure was analyzed. The membrane pervaporation performance was evaluated by varying the PVA content, the annealing temperature, feed concentration and operation temperature. The membrane exhibited a fairly good ethanol dehydration capacity and long-term operational stability.展开更多
The interfacial compatibility of composite membrane is an important factor to its structural stability, andseparation performance. In this study, poly （ether sulfone） （PES） support layer was first hydrophilically ...The interfacial compatibility of composite membrane is an important factor to its structural stability, andseparation performance. In this study, poly （ether sulfone） （PES） support layer was first hydrophilically modified with poly（vinyl alcohol） （PVA） via surface segregation during the phase inversion process. Gelatin （GE） was then cast on the PVA-modified PES support layer as the active layer followed by crosslinking to fabricate composite membranes for ethanol dehydration. The enrichment of PVA on the surface of support layer improved interfacial compatibility of the as-prepared GE/PVA-PES composite membrane. The water contact angle measurement and X-ray photoelectron spectroscopy （XPS） data confirmed the surface segregation of PVA with a surface coverage density of -80%. T-peel test showed that the maxima/force to separate the support layer and the active layer was enhanced by 3 times compared with the GE/PES membrane. The effects of PVA content in the support layer, crosslinking of GE active layer and operating parameters on the pervaporative dehydration performance were investigated. The operational stability of the composite membrane was tested by immersing the membrane in ethanol aqueous solution for a period of time. Stable pervaporation performance for dehydration of 90% ethanol solution was obtained for GE/PVA-PES membrane with a separation factor of -60 and a permeation flux of -1910 g.m^-2.h1 without peeling over 28 days immersion.展开更多
A high performance composite membrane was prepared under the inspiration of bioadhesion principles for pervaporative dehydration of ethanol.Chitosan(CS)and polyacrylonitrile(PAN)ultrafiltration membranes were used as ...A high performance composite membrane was prepared under the inspiration of bioadhesion principles for pervaporative dehydration of ethanol.Chitosan(CS)and polyacrylonitrile(PAN)ultrafiltration membranes were used as the active layer and the support layer,respectively.Guar gum(GG),a natural bioadhesive,was introduced as the intermediate bonding layer to improve the separation performance and stability of the fabricated CS/GG/PAN composite membranes.The contact angle of the GG layer was just between those of the CS layer and the PAN layer,minimizing the difference of hydrophilicity between the active layer and the support layer.The peeling strength of the composite membrane was significantly enhanced after the introduction of the GG layer.The effects of preparation conditions and operation conditions including GG concentration,operating temperature and ethanol concentration in feed on the pervaporation performance were investigated.The as-fabricated CS/GG/PAN composite membrane showed the optimum performance with a permeation flux of up to804 g·m-2·h-1and a separation factor higher than 1900.Besides,the composite membranes exhibited a desirable long-term operational stability.展开更多
基金Supported by the State Key Development Program for Basic Research of China (2009CB623404)Program for New Century Excellent Talents in University,the Programme of Introducing Talents of Discipline to Universities (B06006)State KeyLaboratory for Modification of Chemical Fibers and Polymer Materials (Dong Hua University)
文摘A facile surface segregation method was utilized to fabricate poly（vinyl alcohol）-polyethersulfone （PVA-PES） composite membranes. PVA and PES were first dissolved in dimethyl sulfoxide （DMSO）, then casted on a glass plate and immersed in a coagulation bath. During the phase inversion process in coagulation bath, PVA spontaneously segregated to the polymer solution/coagulation bath interface. The enriched PVA on the surface was further crosslinked by glutaraldehyde. Scanning electron microscopy （SEM）, X-ray photoelectron spectroscopy （XPS） and energy dispersive spectrometer （EDS） confirmed the integral and asymmetric membrane structure with a dense PVA-enriched surface and a porous PES-enriched support, as well as the surface enrichment of PVA. The coverage fraction of the membrane surtace by PVA reacned up to 86.8% when me PVA content m me membrane recipe was 16.7% （by mass）. The water contact angle decreased with the increase of PVA content. The effect of coagulation bath type on membrane structure was analyzed. The membrane pervaporation performance was evaluated by varying the PVA content, the annealing temperature, feed concentration and operation temperature. The membrane exhibited a fairly good ethanol dehydration capacity and long-term operational stability.
基金Supported by the New Century Excellent Talents in University(NCET-10-0623)National Natural Science Foundation for Distinguished Young Scholars(21125627)+1 种基金National Basic Research Program of China(2009CB623404)State Key Laboratory for Modification of Chemical Fibers and Polymer Materials(Dong Hua University)
文摘The interfacial compatibility of composite membrane is an important factor to its structural stability, andseparation performance. In this study, poly （ether sulfone） （PES） support layer was first hydrophilically modified with poly（vinyl alcohol） （PVA） via surface segregation during the phase inversion process. Gelatin （GE） was then cast on the PVA-modified PES support layer as the active layer followed by crosslinking to fabricate composite membranes for ethanol dehydration. The enrichment of PVA on the surface of support layer improved interfacial compatibility of the as-prepared GE/PVA-PES composite membrane. The water contact angle measurement and X-ray photoelectron spectroscopy （XPS） data confirmed the surface segregation of PVA with a surface coverage density of -80%. T-peel test showed that the maxima/force to separate the support layer and the active layer was enhanced by 3 times compared with the GE/PES membrane. The effects of PVA content in the support layer, crosslinking of GE active layer and operating parameters on the pervaporative dehydration performance were investigated. The operational stability of the composite membrane was tested by immersing the membrane in ethanol aqueous solution for a period of time. Stable pervaporation performance for dehydration of 90% ethanol solution was obtained for GE/PVA-PES membrane with a separation factor of -60 and a permeation flux of -1910 g.m^-2.h1 without peeling over 28 days immersion.
基金Supported by the New Century Excellent Talents in University(NCET-10-0623)the National Natural Science Foundation for Distinguished Young Scholars(21125627)+1 种基金the National Basic Research Program of China(2009CB623404)State Key Laboratory for Modification of Chemical Fibers and Polymer Materials(Dong Hua University)
文摘A high performance composite membrane was prepared under the inspiration of bioadhesion principles for pervaporative dehydration of ethanol.Chitosan(CS)and polyacrylonitrile(PAN)ultrafiltration membranes were used as the active layer and the support layer,respectively.Guar gum(GG),a natural bioadhesive,was introduced as the intermediate bonding layer to improve the separation performance and stability of the fabricated CS/GG/PAN composite membranes.The contact angle of the GG layer was just between those of the CS layer and the PAN layer,minimizing the difference of hydrophilicity between the active layer and the support layer.The peeling strength of the composite membrane was significantly enhanced after the introduction of the GG layer.The effects of preparation conditions and operation conditions including GG concentration,operating temperature and ethanol concentration in feed on the pervaporation performance were investigated.The as-fabricated CS/GG/PAN composite membrane showed the optimum performance with a permeation flux of up to804 g·m-2·h-1and a separation factor higher than 1900.Besides,the composite membranes exhibited a desirable long-term operational stability.