TiO2 nanotubes were prepared under normal pressure at a temperature of 120 ℃. Ag, Au, Pt nanoparticles supported on TiO2 nanotubes were prepared by m icrowave assisted heating polyol process. TEM images showed that m...TiO2 nanotubes were prepared under normal pressure at a temperature of 120 ℃. Ag, Au, Pt nanoparticles supported on TiO2 nanotubes were prepared by m icrowave assisted heating polyol process. TEM images showed that microwave prepa red Ag, Au, Pt nanoparticles supported on TiO2 nanotubes were small and well dis persed on the surface of the TiO2 nanotubes. UV-Vis absorption spectra showed th at the absorbance of Ag/TiO2 nanotubes and Au/TiO2 nanotubes in the visible ligh t range increased greatly compared to the single titania nanotubes.展开更多
Using Fe doped titania powders as the precursor, Fe doped TiO2 nanotubes with small diameter of 10nm were obtained by hydrothermal method. The doped titania powders have two different crystalline phases, anatase and r...Using Fe doped titania powders as the precursor, Fe doped TiO2 nanotubes with small diameter of 10nm were obtained by hydrothermal method. The doped titania powders have two different crystalline phases, anatase and rutile of which the average particle diameters are 30.3nm and 41.7nm, receptively. The products were characterized by TEM, XRD and EDS. The results showed that Fe doped TiO2 nanotubes of 200nm in length could be obtained from Fe doped rutile powder, and have higher yields. The formation mechanism of long titania nanotubes was suggested in the light of the relative stability of crystalline phase.展开更多
Spherical calcium carbonate was prepared by the reaction of sodium carbonate with calcium chloride at the presence of a protein like molecule, polyvinylpyrrolidone, as the template. The products were characterized by ...Spherical calcium carbonate was prepared by the reaction of sodium carbonate with calcium chloride at the presence of a protein like molecule, polyvinylpyrrolidone, as the template. The products were characterized by elemental analyses, XRD, SEM, and TG DSC respectively. The effects of polyvinylpyrrolidone on the crystal form and morphology of the as prepared CaCO3 were investigated. It was found that the aggregative shape of the produced calcium carbonate crystalline could be well controlled by adjusting the concentration of the polyvinylpyrrolidone template. This may be of important meanings to the biomimetic synthesis of novel inorganic materials.展开更多
The iron doping titanium dioxide was prepared by sol-gel,step precipitation,co-precipitation and immersion methods,respectively.The photocatalytic activities of these prepared samples were evaluated in X-3B dispersion...The iron doping titanium dioxide was prepared by sol-gel,step precipitation,co-precipitation and immersion methods,respectively.The photocatalytic activities of these prepared samples were evaluated in X-3B dispersion irradiated under UV.The experimental results showed that the immersion method,especially using the nano TiO2 as immersion matrix,greatly enhanced the photocatalytic activity.One fold enhancement in photocatalytic activity was observed in the case of the sample prepared by immersion doping method.This may be attributed to the nano-size effect,the irreversible hole trapper in non-saturated bonding field of Fe3＋ and larger lattice strain.展开更多
用化学复合镀技术制备了含有无机类富勒烯硫化钨纳米材料的Ni P (IF WS2 )复合镀层 .用环 -块摩擦实验测试了Ni P (IF WS2 )的摩擦学性能 .研究结果表明它比与Ni P ,Ni P (层状 2H WS2 )和Ni P 石墨复合镀层具有更高的耐磨性能和更低的...用化学复合镀技术制备了含有无机类富勒烯硫化钨纳米材料的Ni P (IF WS2 )复合镀层 .用环 -块摩擦实验测试了Ni P (IF WS2 )的摩擦学性能 .研究结果表明它比与Ni P ,Ni P (层状 2H WS2 )和Ni P 石墨复合镀层具有更高的耐磨性能和更低的摩擦系数 .分析了无机类富勒烯纳米材料改善镀层摩擦学性能的机理 .展开更多
The effect of Lanthanum content,calcinating temperature and calcinating time on the photocatalytic activity of Lanthanum doping TiO 2 was investigated.The study showed that samples treated under higher temperature and...The effect of Lanthanum content,calcinating temperature and calcinating time on the photocatalytic activity of Lanthanum doping TiO 2 was investigated.The study showed that samples treated under higher temperature and longer calcinating time exhibited higher photocatalytic activity.The X ray diffraction pattern revealed that the lattice of those samples was highly expanded.It is suggested that the highly distorted crystal lattice may be involved in producing more ways by which the hole was captured.Thus,the photocatalytic activity of samples treated under higher temperature and longer time was promoted.展开更多
文摘TiO2 nanotubes were prepared under normal pressure at a temperature of 120 ℃. Ag, Au, Pt nanoparticles supported on TiO2 nanotubes were prepared by m icrowave assisted heating polyol process. TEM images showed that microwave prepa red Ag, Au, Pt nanoparticles supported on TiO2 nanotubes were small and well dis persed on the surface of the TiO2 nanotubes. UV-Vis absorption spectra showed th at the absorbance of Ag/TiO2 nanotubes and Au/TiO2 nanotubes in the visible ligh t range increased greatly compared to the single titania nanotubes.
文摘Using Fe doped titania powders as the precursor, Fe doped TiO2 nanotubes with small diameter of 10nm were obtained by hydrothermal method. The doped titania powders have two different crystalline phases, anatase and rutile of which the average particle diameters are 30.3nm and 41.7nm, receptively. The products were characterized by TEM, XRD and EDS. The results showed that Fe doped TiO2 nanotubes of 200nm in length could be obtained from Fe doped rutile powder, and have higher yields. The formation mechanism of long titania nanotubes was suggested in the light of the relative stability of crystalline phase.
文摘Spherical calcium carbonate was prepared by the reaction of sodium carbonate with calcium chloride at the presence of a protein like molecule, polyvinylpyrrolidone, as the template. The products were characterized by elemental analyses, XRD, SEM, and TG DSC respectively. The effects of polyvinylpyrrolidone on the crystal form and morphology of the as prepared CaCO3 were investigated. It was found that the aggregative shape of the produced calcium carbonate crystalline could be well controlled by adjusting the concentration of the polyvinylpyrrolidone template. This may be of important meanings to the biomimetic synthesis of novel inorganic materials.
文摘The iron doping titanium dioxide was prepared by sol-gel,step precipitation,co-precipitation and immersion methods,respectively.The photocatalytic activities of these prepared samples were evaluated in X-3B dispersion irradiated under UV.The experimental results showed that the immersion method,especially using the nano TiO2 as immersion matrix,greatly enhanced the photocatalytic activity.One fold enhancement in photocatalytic activity was observed in the case of the sample prepared by immersion doping method.This may be attributed to the nano-size effect,the irreversible hole trapper in non-saturated bonding field of Fe3＋ and larger lattice strain.
文摘用化学复合镀技术制备了含有无机类富勒烯硫化钨纳米材料的Ni P (IF WS2 )复合镀层 .用环 -块摩擦实验测试了Ni P (IF WS2 )的摩擦学性能 .研究结果表明它比与Ni P ,Ni P (层状 2H WS2 )和Ni P 石墨复合镀层具有更高的耐磨性能和更低的摩擦系数 .分析了无机类富勒烯纳米材料改善镀层摩擦学性能的机理 .
文摘The effect of Lanthanum content,calcinating temperature and calcinating time on the photocatalytic activity of Lanthanum doping TiO 2 was investigated.The study showed that samples treated under higher temperature and longer calcinating time exhibited higher photocatalytic activity.The X ray diffraction pattern revealed that the lattice of those samples was highly expanded.It is suggested that the highly distorted crystal lattice may be involved in producing more ways by which the hole was captured.Thus,the photocatalytic activity of samples treated under higher temperature and longer time was promoted.