Surface roughness is an important factor that affects the wetting of molten metal on ceramics.The effect of surface roughness of the alumina substrate on the contact angle,contact diameter,drop height and surface tens...Surface roughness is an important factor that affects the wetting of molten metal on ceramics.The effect of surface roughness of the alumina substrate on the contact angle,contact diameter,drop height and surface tension of molten lead was investigated in the temperature range of 923-1123 K.The microstructure of the lead/substrate interface was observed by SEM.The surface free energy of alumina substrates was calculated by the geometrical average method.When the surface roughness of the substrate increased from 0.092 to 2.23μm,the surface free energy increased gradually,ranging from 13.356 to 39.998 mJ/m^(2).The contact diameter of lead droplets decreased from 9.111 to 7.19 mm.The lead drop height increased from 3.41 to 3.85 mm.The contact angle increased from 113.05°to 137.15°.Moreover,the surface depression of the alumina substrate was filled with lead,and no obvious change was observed.The results demonstrated that the wetting of lead drop on alumina substrates was consistent with the Wenzel state.展开更多
Slag movement on SiO2-based prism refractories in different slag systems was observed. The cross section shape evolution mechanism was discussed. Two types of shape evolution appear. For PbO-SiO2 slag whose surface te...Slag movement on SiO2-based prism refractories in different slag systems was observed. The cross section shape evolution mechanism was discussed. Two types of shape evolution appear. For PbO-SiO2 slag whose surface tension improves with SiO2 concentration, slag film flows up along four edges under axial Marangoni shear force and wettability. Then, it flows down along four lateral faces under gravity. Corrosion rate at edges is larger than that on lateral faces due to different SiO2 solubilities of ascending and descending flow. Prism cross section shape changes from square to round. For FetO-SiO2 slag whose surface tension reduces with the increase of SiO2 concentration, slag film flows up under the inflence of wettability. Then, it flows down under Marangoni shear force and gravity. Compared to four edges, slag is mainly up and down on four lateral faces due to larger surface tension and size. So, prism cross section shape keeps square.展开更多
基金financial supports from the National Natural Science Foundation of China(Nos.51974022,U1738101)Fundamental Research Funds for the Central Universities,China(No.FRF-MP-20-17)。
文摘Surface roughness is an important factor that affects the wetting of molten metal on ceramics.The effect of surface roughness of the alumina substrate on the contact angle,contact diameter,drop height and surface tension of molten lead was investigated in the temperature range of 923-1123 K.The microstructure of the lead/substrate interface was observed by SEM.The surface free energy of alumina substrates was calculated by the geometrical average method.When the surface roughness of the substrate increased from 0.092 to 2.23μm,the surface free energy increased gradually,ranging from 13.356 to 39.998 mJ/m^(2).The contact diameter of lead droplets decreased from 9.111 to 7.19 mm.The lead drop height increased from 3.41 to 3.85 mm.The contact angle increased from 113.05°to 137.15°.Moreover,the surface depression of the alumina substrate was filled with lead,and no obvious change was observed.The results demonstrated that the wetting of lead drop on alumina substrates was consistent with the Wenzel state.
基金Projects(U1738101,51804023)supported by the National Natural Science Foundation of ChinaProjects(FRF-TP-18-007A1,FRF-MP-18-007)supported by Fundamental Research Funds for the Central Universities,ChinaProject(2019M650489)supported by China Postdoctoral Science Foundation
文摘Slag movement on SiO2-based prism refractories in different slag systems was observed. The cross section shape evolution mechanism was discussed. Two types of shape evolution appear. For PbO-SiO2 slag whose surface tension improves with SiO2 concentration, slag film flows up along four edges under axial Marangoni shear force and wettability. Then, it flows down along four lateral faces under gravity. Corrosion rate at edges is larger than that on lateral faces due to different SiO2 solubilities of ascending and descending flow. Prism cross section shape changes from square to round. For FetO-SiO2 slag whose surface tension reduces with the increase of SiO2 concentration, slag film flows up under the inflence of wettability. Then, it flows down under Marangoni shear force and gravity. Compared to four edges, slag is mainly up and down on four lateral faces due to larger surface tension and size. So, prism cross section shape keeps square.