YAG： 1% （atom fraction） Yb^3＋ , 0.5% （atom fraction） Er3＋ transparent ceramics were fabricated by the solid state reaction method using high-purity Y2O3, Al2O3, Yb2O3, and Er2O3 powders as starting materials. T...YAG： 1% （atom fraction） Yb^3＋ , 0.5% （atom fraction） Er3＋ transparent ceramics were fabricated by the solid state reaction method using high-purity Y2O3, Al2O3, Yb2O3, and Er2O3 powders as starting materials. The mixed powder compact was sintered at 1760 ℃ for 6 h in vacuum and annealed at 1500 ℃ for 10 h in an air atmosphere. The ceramics consisted of about 10μm grains and exhibited a pore-free structure. The optical transmittance of the ceramics at 1064 nm was nearly 80%. Upconversion emissions were investigated on the ceramics pumped by a 980 nm continuous wave diode laser, and strong green emission centered at 523 and 559 nm and red emission centered at 669 nm were observed, which originated from the radiative transitions of ^2H11/2→^4I15/2, ^4S3/2→^4I15/2, and ^4F9/2→^4I15/2 of Er^3＋ ions, respectively.展开更多
基金Project supported bythe National Natural Science Foundation of China (50372075)
文摘YAG： 1% （atom fraction） Yb^3＋ , 0.5% （atom fraction） Er3＋ transparent ceramics were fabricated by the solid state reaction method using high-purity Y2O3, Al2O3, Yb2O3, and Er2O3 powders as starting materials. The mixed powder compact was sintered at 1760 ℃ for 6 h in vacuum and annealed at 1500 ℃ for 10 h in an air atmosphere. The ceramics consisted of about 10μm grains and exhibited a pore-free structure. The optical transmittance of the ceramics at 1064 nm was nearly 80%. Upconversion emissions were investigated on the ceramics pumped by a 980 nm continuous wave diode laser, and strong green emission centered at 523 and 559 nm and red emission centered at 669 nm were observed, which originated from the radiative transitions of ^2H11/2→^4I15/2, ^4S3/2→^4I15/2, and ^4F9/2→^4I15/2 of Er^3＋ ions, respectively.