This investigation deals with the free radical polymerization both of (2-methacryloyloxyethyl) trimethyl ammonium chloride (QACEMA) and of diallyldimethyl ammonium chloride (DADMAC) in inverse emulsion. The influences...This investigation deals with the free radical polymerization both of (2-methacryloyloxyethyl) trimethyl ammonium chloride (QACEMA) and of diallyldimethyl ammonium chloride (DADMAC) in inverse emulsion. The influences of some factors, such as the concentration of monomers, initiator and emulsifier are discussed. The polymerization rate equations of above two monomers can be written as follows: R(p) = k[M](1.21)[I](0.82)[E](0.57) (for QACEMA) R(p) = k'[M](1.34)[I](0.90)[E](0.62) (for DADMAC)展开更多
The selective water plugging agent was prepared by heating the blends of the polyacry-lamide inverse latex, modified urea formaldehyde resin, crosslinking agent and catalysts.The results show that using different type...The selective water plugging agent was prepared by heating the blends of the polyacry-lamide inverse latex, modified urea formaldehyde resin, crosslinking agent and catalysts.The results show that using different types of polymers and additives or changing in theirproportion of the blends, the gelling viscosity, starting point of gelling and other propertiesof the IPN can be controlled.展开更多
基金This project is supported by Tianjin Science Foundation for Youths.
文摘This investigation deals with the free radical polymerization both of (2-methacryloyloxyethyl) trimethyl ammonium chloride (QACEMA) and of diallyldimethyl ammonium chloride (DADMAC) in inverse emulsion. The influences of some factors, such as the concentration of monomers, initiator and emulsifier are discussed. The polymerization rate equations of above two monomers can be written as follows: R(p) = k[M](1.21)[I](0.82)[E](0.57) (for QACEMA) R(p) = k'[M](1.34)[I](0.90)[E](0.62) (for DADMAC)
文摘The selective water plugging agent was prepared by heating the blends of the polyacry-lamide inverse latex, modified urea formaldehyde resin, crosslinking agent and catalysts.The results show that using different types of polymers and additives or changing in theirproportion of the blends, the gelling viscosity, starting point of gelling and other propertiesof the IPN can be controlled.